Investigation of stress corrosion cracking Behaviors of an AZ91 magnesium alloy in 0.1 kmol/m(3) Na2SO4 solution using slow strain rate test
文献类型：期刊论文
| 作者 | J. Q. Wang ; J. Chen ; E. H. Han ; W. Ke |
| 刊名 | Materials Transactions
 |
| 出版日期 | 2008 |
| 卷号 | 49期号:5页码:1052-1056 |
| 关键词 | AZ91 magnesium alloy stress corrosion cracking slow strain rate test hydrogen embrittlement sodium-sulfate solution mechanism |
| ISSN号 | 1345-9678 |
| 中文摘要 | The stress corrosion cracking (SCC) behavior of an as-cast AZ91 magnesium alloy in 0.1 kmol/m(3) Na2SO4 solution was investigated using slow strain rate test (SSRT). The results showed that both the uncharged and charged AZ91 alloy occurred transgranular stress corrosion cracking (TGSCC), which were characteristic of large-plane cleavage fracture. Pre-charging had little influences on mechanical properties. It indicated that hydrogen embrittlement (HE) was the main mechanism for the SCC of AZ91 alloy in 0.1 kmol/m(3) Na2SO4 solution. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/33133]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. Q. Wang,J. Chen,E. H. Han,et al. Investigation of stress corrosion cracking Behaviors of an AZ91 magnesium alloy in 0.1 kmol/m(3) Na2SO4 solution using slow strain rate test[J]. Materials Transactions,2008,49(5):1052-1056. |
| APA | J. Q. Wang,J. Chen,E. H. Han,&W. Ke.(2008).Investigation of stress corrosion cracking Behaviors of an AZ91 magnesium alloy in 0.1 kmol/m(3) Na2SO4 solution using slow strain rate test.Materials Transactions,49(5),1052-1056. |
| MLA | J. Q. Wang,et al."Investigation of stress corrosion cracking Behaviors of an AZ91 magnesium alloy in 0.1 kmol/m(3) Na2SO4 solution using slow strain rate test".Materials Transactions 49.5(2008):1052-1056. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。