Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature
文献类型：期刊论文
| 作者 | Y. M. Xiong ; S. L. Zhu ; F. H. Wang |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2008 |
| 卷号 | 50期号:1页码:15-22 |
| 关键词 | titanium metal coatings X-ray diffraction high temperature corrosion oxide coatings alumina scale formation oxide hydroxide evaporation al-cr alloys oxidation behavior water-vapor titanium aluminides cyclic oxidation coatings chromium intermetallics |
| ISSN号 | 0010-938X |
| 中文摘要 | In the present paper, the corrosion behavior of Ti60 alloys with an aluminide, TiAlCr, and enamel coatings in moist air containing NaCl vapor at 700-800 degrees C were studied. The results showed that the TiAlCr and aluminide coatings failed to protect the substrate from corrosion due to the cyclic formation of volatile products during corrosion at 800 degrees C. However, an uneven continuous protective Al2O3 scale could form on the aluminide coating during corrosion at 700 degrees C. And the enamel coating could protect Ti60 from corrosion due to its high thermochernical stability and matched thermal expansion coefficient with substrates of Ti-base alloys during corrosion. (c) 2007 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/33238]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. M. Xiong,S. L. Zhu,F. H. Wang. Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature[J]. Corrosion Science,2008,50(1):15-22. |
| APA | Y. M. Xiong,S. L. Zhu,&F. H. Wang.(2008).Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature.Corrosion Science,50(1),15-22. |
| MLA | Y. M. Xiong,et al."Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature".Corrosion Science 50.1(2008):15-22. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。