Fracture behavior of Zr55Cu30Al10Ni5 bulk metallic glass under quasi-static and dynamic compression
文献类型：期刊论文
| 作者 | R. Q. Yang ; J. T. Fan ; S. X. Li ; Z. F. Zhang |
| 刊名 | Journal of Materials Research
 |
| 出版日期 | 2008 |
| 卷号 | 23期号:6页码:1744-1750 |
| 关键词 | ni-cu-be amorphous-alloys plastic-flow strain-rate hydrostatic-pressure deformation-behavior toughness dependence mechanism strength |
| ISSN号 | 0884-2914 |
| 中文摘要 | Fracture behavior of Zr55Cu30Al10Ni5 bulk metallic glass was investigated under quasi-static compression at strain rate of 10(-4)/s using an Instron testing machine and dynamic split Hopkinson bar (SHPB) compression with strain rate of about 1900-4300/s. Pronounced strain softening, especially past the peak stress, was observed under SHPB tests and compared with the distinct flow serrations under quasi-static tests. Scanning electron microscope revealed that the angle between the loading axis and major shear plane is less than 45 degrees, deviating from the maximum shear stress plane. Microscopically, unlike the ordinary veinlike pattern found in quasi-static compression, the elongated veinlike pattern was observed at the onset position of rapid shearing under dynamic test. A closely arrayed dendritelike structure dominated the dynamic fracture, consequently, and should be the major pattern representing the rapid shear band propagation. In addition, a transition state from veinlike to dendritelike pattern was observed at the final instantaneous fracture region in quasi-static tests. Evidence revealed the characteristic dimension of dynamic fracture surface complies with Taylor's meniscus instability criterion. The roles of free volume and adiabatic heating on the fracture strength and stress concentration on the fracture morphology are also discussed. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/33276]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | R. Q. Yang,J. T. Fan,S. X. Li,et al. Fracture behavior of Zr55Cu30Al10Ni5 bulk metallic glass under quasi-static and dynamic compression[J]. Journal of Materials Research,2008,23(6):1744-1750. |
| APA | R. Q. Yang,J. T. Fan,S. X. Li,&Z. F. Zhang.(2008).Fracture behavior of Zr55Cu30Al10Ni5 bulk metallic glass under quasi-static and dynamic compression.Journal of Materials Research,23(6),1744-1750. |
| MLA | R. Q. Yang,et al."Fracture behavior of Zr55Cu30Al10Ni5 bulk metallic glass under quasi-static and dynamic compression".Journal of Materials Research 23.6(2008):1744-1750. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。