Effect of annealing treatment on the oxidation of an electrodeposited alumina-forming Ni-Al nanocomposite
文献类型:期刊论文
作者 | X. Yang ; X. Peng ; F. Wang |
刊名 | Corrosion Science
![]() |
出版日期 | 2008 |
卷号 | 50期号:11页码:3227-3232 |
关键词 | Metal matrix composites X-ray diffraction TEM SEM Selective oxidation composite coatings cyclic oxidation cr nanocomposite film 1050-degrees-c particles corrosion behavior |
ISSN号 | 0010-938X |
中文摘要 | An electrodeposited alumina-forming Ni-Al nanocomposite having a nanocrystalline Ni matrix dispersing Al nanoparticles was annealed in vacuum at 600 degrees C, leading to coarsened Ni grains that were doped with a certain amount of Al atoms diffused from the nanoparticles. Oxidation in air at 1000 IC indicated that the annealing decreased the oxidation of the nanocomposite, due to a promotion in the formation of a protective alumina layer. A progressive-oxidation mode demonstrating the competing growth of alumina on the as-deposited and annealed nanocomposites was proposed, as an explanation of the accelerated development of the alumina layer on the annealed nanocomposite. (C) 2008 Elsevier Ltd. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
源URL | [http://210.72.142.130/handle/321006/33278] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | X. Yang,X. Peng,F. Wang. Effect of annealing treatment on the oxidation of an electrodeposited alumina-forming Ni-Al nanocomposite[J]. Corrosion Science,2008,50(11):3227-3232. |
APA | X. Yang,X. Peng,&F. Wang.(2008).Effect of annealing treatment on the oxidation of an electrodeposited alumina-forming Ni-Al nanocomposite.Corrosion Science,50(11),3227-3232. |
MLA | X. Yang,et al."Effect of annealing treatment on the oxidation of an electrodeposited alumina-forming Ni-Al nanocomposite".Corrosion Science 50.11(2008):3227-3232. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。