YSurface alloying of Mg alloys after surface nanocrystallization
文献类型：期刊论文
| 作者 | M. X. Zhang ; Y. N. Shi ; H. Q. Sun ; P. M. Kelly |
| 刊名 | Journal of Nanoscience and Nanotechnology
 |
| 出版日期 | 2008 |
| 卷号 | 8期号:5页码:2724-2728 |
| 关键词 | magnesium alloys surface nanocrystallization surface alloying mechanical attrition treatment induced grain-refinement az91d magnesium alloy precipitate morphology layer |
| ISSN号 | 1533-4880 |
| 中文摘要 | Surface nanocrystallization using a surface mechanical attrition treatment effectively activates the surface of magnesium alloys due to the increase in grain boundary diffusion channels. As a result, the temperature of subsequent surface alloying treatment of pure Mg and AZ91 alloy can be reduced from 430 degrees C to 380 degrees C. Thus, it is possible to combine the surface alloying process with the solution treatment for this type of alloy. After surface alloying, the hardness of the alloyed layer is 3 to 4 times higher than that of the substrate and this may significantly improve the wear resistance of magnesium alloys. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33329]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | M. X. Zhang,Y. N. Shi,H. Q. Sun,et al. YSurface alloying of Mg alloys after surface nanocrystallization[J]. Journal of Nanoscience and Nanotechnology,2008,8(5):2724-2728. |
| APA | M. X. Zhang,Y. N. Shi,H. Q. Sun,&P. M. Kelly.(2008).YSurface alloying of Mg alloys after surface nanocrystallization.Journal of Nanoscience and Nanotechnology,8(5),2724-2728. |
| MLA | M. X. Zhang,et al."YSurface alloying of Mg alloys after surface nanocrystallization".Journal of Nanoscience and Nanotechnology 8.5(2008):2724-2728. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。