Fabrication and characterization of cellular iron nanocrystalline film
文献类型：期刊论文
| 作者 | W. Zhang ; Z. Q. Liu ; K. Furuya |
| 刊名 | Nanotechnology
 |
| 出版日期 | 2008 |
| 卷号 | 19期号:13 |
| 关键词 | beam-induced deposition tungsten nanowire nanoparticles |
| ISSN号 | 0957-4484 |
| 中文摘要 | Cellular iron nanocrystalline film was fabricated on carbon substrate by electron beam chemical vapor deposition (EB-CVD). The film was made up of single alpha-iron cubes with {100} facets ranging from several tens to 200 nm. The thickness and distribution of the film could be controlled by adjusting the irradiation position and duration of the electron beam. The integration of well-faceted nanocrystals enables the film to have a high ratio of free surfaces, which are essential for applications in chemical catalysis and energy absorption. The application of this film as a substrate for further nanofabrication was demonstrated. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/33342]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | W. Zhang,Z. Q. Liu,K. Furuya. Fabrication and characterization of cellular iron nanocrystalline film[J]. Nanotechnology,2008,19(13). |
| APA | W. Zhang,Z. Q. Liu,&K. Furuya.(2008).Fabrication and characterization of cellular iron nanocrystalline film.Nanotechnology,19(13). |
| MLA | W. Zhang,et al."Fabrication and characterization of cellular iron nanocrystalline film".Nanotechnology 19.13(2008). |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。