Initial corrosion behavior of AZ91 magnesium alloy in simulating acid rain under wet-dry cyclic condition
文献类型：期刊论文
| 作者 | W. Q. Zhou ; D. Y. Shan ; E. H. Han ; W. Ke |
| 刊名 | Transactions of Nonferrous Metals Society of China
 |
| 出版日期 | 2008 |
| 卷号 | 18页码:S334-S338 |
| 关键词 | magnesium alloy atmospheric corrosion simulating acid rain wet-dry cycle atmospheric corrosion chloride |
| ISSN号 | 1003-6326 |
| 中文摘要 | Corrosion behavior of AZ91 magnesium alloy in simulating acid rain under wet-dry cyclic condition was investigated. The results show that corrosion potential shifts positively and the corrosion current density decreases at low wet-dry cyclic time. Further increase of the cyclic time results in the negative movement of corrosion potential and the increase of current density. SEM observation indicates that corrosion occurs only in a phase, P phase is inert in corrosive medium, and the corrosion of AZ91 magnesium appears in uniform characteristic. XPS analysis suggests that the corrosion product is mainly composed of oxide and hydroxide of magnesium and aluminum, and a small amount of sulfate is also contained in the film. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/33394]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | W. Q. Zhou,D. Y. Shan,E. H. Han,et al. Initial corrosion behavior of AZ91 magnesium alloy in simulating acid rain under wet-dry cyclic condition[J]. Transactions of Nonferrous Metals Society of China,2008,18:S334-S338. |
| APA | W. Q. Zhou,D. Y. Shan,E. H. Han,&W. Ke.(2008).Initial corrosion behavior of AZ91 magnesium alloy in simulating acid rain under wet-dry cyclic condition.Transactions of Nonferrous Metals Society of China,18,S334-S338. |
| MLA | W. Q. Zhou,et al."Initial corrosion behavior of AZ91 magnesium alloy in simulating acid rain under wet-dry cyclic condition".Transactions of Nonferrous Metals Society of China 18(2008):S334-S338. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。