Protective properties of high temperature oxide films on Ni-based superalloys in 3.5% NaCl solution
文献类型：期刊论文
| 作者 | H. P. Bai ; F. H. Fang |
| 刊名 | Journal of Materials Science & Technology
 |
| 出版日期 | 2007 |
| 卷号 | 23期号:4页码:541-546 |
| 关键词 | high temperature oxide film protective properties EIS Mott-Schottky analysis electrochemical-impedance spectroscopy zinc-based coatings pvd coated steels corrosion behavior stainless-steels passive film electronic-structure oxidation behavior aqueous-solution part ii |
| ISSN号 | 1005-0302 |
| 中文摘要 | The electrochemical behaviors of high temperature oxide film formed on the sputtered microcrystalline coating of M38 alloy (mc-M38) were investigated by potentiodynamic and electrochemical impedance spectroscopy (EIS) techniques in 3.5% NaCl solution. Mott-Schottky analysis was used to study the semi-conductive properties of the surface oxide. The results of the capacitance measurements showed that the oxide films on both the coating and the cast alloy were p-type semiconducting characteristics. Both the carrier density (N-a) and the flat band potential (E-fb) were obviously frequency-dependent, and the optimal frequency range was from 1000 to 1500 Hz. The oxidized coating exhibited higher protectivity than the oxidized cast alloy due to the lower carrier density compared with that of the oxidized cast alloy. The EIS data of the long-term immersing tests suggested that the oxide film served as an inner-barrier layer against chloride ions. The penetration of the aggressive ions into the surface oxide resulted in the decreased polarization resistance as a function of the immersion time. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33424]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | H. P. Bai,F. H. Fang. Protective properties of high temperature oxide films on Ni-based superalloys in 3.5% NaCl solution[J]. Journal of Materials Science & Technology,2007,23(4):541-546. |
| APA | H. P. Bai,&F. H. Fang.(2007).Protective properties of high temperature oxide films on Ni-based superalloys in 3.5% NaCl solution.Journal of Materials Science & Technology,23(4),541-546. |
| MLA | H. P. Bai,et al."Protective properties of high temperature oxide films on Ni-based superalloys in 3.5% NaCl solution".Journal of Materials Science & Technology 23.4(2007):541-546. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。