Plasma electrolytic oxidation of AZ91D magnesium alloy with different additives and its corrosion behavior

文献类型:期刊论文

作者F. H. Cao ; J. L. Cao ; Z. Zhang ; J. Q. Zhang ; C. N. Cao
刊名Materials and Corrosion-Werkstoffe Und Korrosion
出版日期2007
卷号58期号:9页码:676-683
关键词ac-impedance measurements oxide-films aluminum coatings
ISSN号0947-5117
中文摘要Plasma electrolytic oxidation (PEO) of Mg-based AZ91D alloys was investigated using 50 Hz AC anodizing technique in an alkaline borate solution, which contained a new kind of organic additive and without F, P, and Cr. The anodizing technological parameters have been optimized and a kind of ivory-white smooth anodic film with high corrosion resistance was obtained. It was found that the formation of the anodic films was always coupled with sparking and oxygen evolution, whose intensity changed with the additive and anodizing voltage. All EIS plots have two capacitive loops and one low frequency inductive component. Two capacitive arcs present the barrier and porous layer of the PEO film and the inductive component in the low frequency domain is a complex behavior due to the porous structure connected to the electrolyte.EIS plots and fitting results show that a self-sealing process of the PEO firm with different additives takes place in the beginning of immersion time, then corrosion attack becomes a preponderant process to promote the degradation of the film. Tafel results show that PEO treatment decreases the corrosion current density by four, even five orders of magnitude, while additives content does not affect strongly the electrochemical corrosion behavior. Salt spray test shows that the PEO film formed with NaAlO2 and Na2SiO3 presents good corrosion resistance, over 600 h without any sealing treatment. The difference of corrosion resistance arose by additives examined by electrochemical techniques and salt spray test does not show strict corresponding relationship.
原文出处://WOS:000250149700004
公开日期2012-04-13
源URL[http://ir.imr.ac.cn/handle/321006/33431]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
F. H. Cao,J. L. Cao,Z. Zhang,et al. Plasma electrolytic oxidation of AZ91D magnesium alloy with different additives and its corrosion behavior[J]. Materials and Corrosion-Werkstoffe Und Korrosion,2007,58(9):676-683.
APA F. H. Cao,J. L. Cao,Z. Zhang,J. Q. Zhang,&C. N. Cao.(2007).Plasma electrolytic oxidation of AZ91D magnesium alloy with different additives and its corrosion behavior.Materials and Corrosion-Werkstoffe Und Korrosion,58(9),676-683.
MLA F. H. Cao,et al."Plasma electrolytic oxidation of AZ91D magnesium alloy with different additives and its corrosion behavior".Materials and Corrosion-Werkstoffe Und Korrosion 58.9(2007):676-683.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。