Effect of SDC-impregnated LSM cathodes on the performance of anode-supported YSZ films for SOFCs
文献类型：期刊论文
| 作者 | K. F. Chen ; Z. Lu ; N. Ai ; X. J. Chen ; J. Y. Hu ; X. Q. Huang ; W. H. Su |
| 刊名 | Journal of Power Sources
 |
| 出版日期 | 2007 |
| 卷号 | 167期号:1页码:84-89 |
| 关键词 | La0.7Sr0.3MnO3 (LSM) impregnation SM0.2Ce0.8O1.9 (SDC) concentration polarization mass transfer process oxide fuel-cells doped ceria electrolytes thin-film coating technique low-temperature it-sofcs fabrication electrodes parameters oxygen |
| ISSN号 | 0378-7753 |
| 中文摘要 | Sm0.2Ce0.8O1.9 (SDC)-impregnated La0.7Sr0.3MnO3 (LSM) composite cathodes were fabricated on anode-supported yttria-stabilized zirconia (YSZ) thin films. Electrochemical performances of the solid oxide fuel cells (SOFCs) were investigated in the present study. Four single cells, i.e., Cell-1, Cell-2, Cell-3 and Cell-4 were obtained after the fabrication of four different cathodes, i.e., pure LSM and SDC/LSM composites in the weight ratios of 25/75, 36/64 and 42/58, respectively. Impedance spectra under open-circuit conditions showed that the cathode performance was gradually improved with the increasing SDC loading. Similarly, the maximum power densities (MPD) of the four cells were increased with the SDC amount below 700 degrees C. Whereas, the cell performance of Cell-4 was lower than that of Cell-3 at 800 degrees C, arising from the increased concentration polarization at high current densities. This was caused by the lowered porosity with the impregnation cycle. This disadvantage could be suppressed by lowering the operating temperature or by increasing the oxygen concentration at the cathode side. The ratio of electrode polarization loss in the total voltage drop versus current density showed that the cell performance was primarily determined by the electrode polarization. The contribution of the ohmic resistance was increased when the operating temperature was lowered. When a 100 ml min(-1) oxygen flow was introduced to the cathode side, Cell-3 produced MPDs of 1905, 1587 and 1179 mW cm(-2) at 800, 750 and 700 degrees C, respectively. The high cell outputs demonstrated the merits of the novel and effective SDC-impregnated LSM cathodes. (C) 2007 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33449]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | K. F. Chen,Z. Lu,N. Ai,et al. Effect of SDC-impregnated LSM cathodes on the performance of anode-supported YSZ films for SOFCs[J]. Journal of Power Sources,2007,167(1):84-89. |
| APA | K. F. Chen.,Z. Lu.,N. Ai.,X. J. Chen.,J. Y. Hu.,...&W. H. Su.(2007).Effect of SDC-impregnated LSM cathodes on the performance of anode-supported YSZ films for SOFCs.Journal of Power Sources,167(1),84-89. |
| MLA | K. F. Chen,et al."Effect of SDC-impregnated LSM cathodes on the performance of anode-supported YSZ films for SOFCs".Journal of Power Sources 167.1(2007):84-89. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。