Microstructure and mechanical behavior of NiAl-based alloy prepared by powder metallurgical route
文献类型：期刊论文
| 作者 | K. W. Huai ; J. T. Guo ; Q. Gao ; H. T. Li ; R. Yang |
| 刊名 | Intermetallics
 |
| 出版日期 | 2007 |
| 卷号 | 15期号:5-6页码:749-752 |
| 关键词 | NiAl-based alloy powder metallurgy microstructure mechanical properties at ambient temperature fracture toughness composites fracture |
| ISSN号 | 0966-9795 |
| 中文摘要 | Rapidly solidified NiAl-28Cr-6Mo-B-Dy prealloyed powder doped with Nb powder was consolidated by hot pressing under 1250 degrees C for 30 inin at 30 MPa. The consolidated material exhibited a different microstructure from the original powder, i.e. the NiAl and Cr(Mo) plates in the eutectic cell tend to break down into short platelets or even particles during hot pressing process. The mechanical behaviors at room temperature and at high temperature of consolidated sample from powder alloy were evaluated by three-point bending technique, tensile test and compressive test. The results showed that the hot pressing alloy possessed a reasonable combination of room temperature ductility and toughness, and elevated temperature strength. (c) 2006 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33592]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | K. W. Huai,J. T. Guo,Q. Gao,et al. Microstructure and mechanical behavior of NiAl-based alloy prepared by powder metallurgical route[J]. Intermetallics,2007,15(5-6):749-752. |
| APA | K. W. Huai,J. T. Guo,Q. Gao,H. T. Li,&R. Yang.(2007).Microstructure and mechanical behavior of NiAl-based alloy prepared by powder metallurgical route.Intermetallics,15(5-6),749-752. |
| MLA | K. W. Huai,et al."Microstructure and mechanical behavior of NiAl-based alloy prepared by powder metallurgical route".Intermetallics 15.5-6(2007):749-752. |