Formation mechanism of nanostructures in austenitic stainless steel during equal channel angular pressing
文献类型：期刊论文
| 作者 | C. X. Huang ; G. Yang ; B. Deng ; S. D. Wu ; S. X. Li ; Z. F. Zhang |
| 刊名 | Philosophical Magazine
 |
| 出版日期 | 2007 |
| 卷号 | 87期号:31页码:4949-4971 |
| 关键词 | severe plastic-deformation stacking-fault energy induced grain-refinement attrition treatment surface-layer zr additions strain-rate transformation evolution copper |
| ISSN号 | 1478-6435 |
| 中文摘要 | An ultra-low carbon austenitic stainless steel was successfully pressed from one to eight passes by equal channel angular pressing (ECAP) at room temperature. By using X-ray diffraction, optical microscopy and transmission electron microscopy, the microstructural evolution during ECAP was investigated to reveal the formation mechanism of strain-induced nanostructures. The refinement mechanism involved the formation of shear bands and deformation twins, followed by the fragmentation of twin lamellae, as well as successive martensite transformation from parent austenitic grains with sizes ranging from microns to nanometres through the processes gamma(fcc)->epsilon(hcp)->alpha'(bcc). After pressing for eight passes, two types of nanocrystalline grains were achieved: ( a) nanocrystalline austenite with a mean grain size of similar to 31nm and (b) strain-induced nanocrystalline alpha'-martensite with a size of similar to 74nm. The formation mechanisms are discussed in terms of microstructural subdivision via deformation twinning and martensite transformation. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33594]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | C. X. Huang,G. Yang,B. Deng,et al. Formation mechanism of nanostructures in austenitic stainless steel during equal channel angular pressing[J]. Philosophical Magazine,2007,87(31):4949-4971. |
| APA | C. X. Huang,G. Yang,B. Deng,S. D. Wu,S. X. Li,&Z. F. Zhang.(2007).Formation mechanism of nanostructures in austenitic stainless steel during equal channel angular pressing.Philosophical Magazine,87(31),4949-4971. |
| MLA | C. X. Huang,et al."Formation mechanism of nanostructures in austenitic stainless steel during equal channel angular pressing".Philosophical Magazine 87.31(2007):4949-4971. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。