Chill-cast in situ composites in the pseudo-ternary Mg-(Cu,Ni)-Y glass-forming system: Microstructure and compressive properties
文献类型：期刊论文
| 作者 | H. Ma ; L. L. Shi ; J. Xu ; E. Ma |
| 刊名 | Journal of Materials Research
 |
| 出版日期 | 2007 |
| 卷号 | 22期号:2页码:314-325 |
| 关键词 | bulk metallic-glass mg-cu-y period ordered structure high-strength mechanical-properties enhanced plasticity matrix composite amorphous-alloys room-temperature ductility |
| ISSN号 | 0884-2914 |
| 中文摘要 | Starting with a bulk metallic glass-forming alloy Mg61Cu18Ni6Y11, we prepared in situ composites by increasing the Mg content in a series of alloys, Mg-x(Cu0.51Ni0.17Y0.32)(100)-x (65 <= x <= 90), via copper mold casting of rods 4 mm in diameter. The fully glassy alloy at x 65 showed a compressive fracture strength of 755 MPa but no observable macroscopic plasticity prior to failure. Metallic glass-based composites were formed when the Mg content was increased. For x > 80, the glassy phase no longer existed in the as-cast rods. In the composition range of 80 <= x <= 85, needle-shaped Mg solution with a 14H-type long period stacking (LPS) structure appeared as the primary phase in the as-cast microstructure. On further increase of the Mg content up to x = 90, the solidified primary phase became 2H-Mg, coexisting with the remaining eutectic structure. The best combination of mechanical properties was obtained for the alloy at x = 81.5, which showed a fracture strength of 665 MPa and a compressive plastic strain of 11.6%. The specific strength of this alloy was 2.8 x 10(5) N m kg(-1), much higher than conventional cast magnesium alloys. The mechanical properties are discussed in light of the phase selection and microstructural features uncovered in microscopy examinations. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33748]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | H. Ma,L. L. Shi,J. Xu,et al. Chill-cast in situ composites in the pseudo-ternary Mg-(Cu,Ni)-Y glass-forming system: Microstructure and compressive properties[J]. Journal of Materials Research,2007,22(2):314-325. |
| APA | H. Ma,L. L. Shi,J. Xu,&E. Ma.(2007).Chill-cast in situ composites in the pseudo-ternary Mg-(Cu,Ni)-Y glass-forming system: Microstructure and compressive properties.Journal of Materials Research,22(2),314-325. |
| MLA | H. Ma,et al."Chill-cast in situ composites in the pseudo-ternary Mg-(Cu,Ni)-Y glass-forming system: Microstructure and compressive properties".Journal of Materials Research 22.2(2007):314-325. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。