Corrosion protection of 304 stainless steel bipolar plates using TiC films produced by high-energy micro-arc alloying process
文献类型：期刊论文
| 作者 | Y. J. Ren ; C. L. Zeng |
| 刊名 | Journal of Power Sources
 |
| 出版日期 | 2007 |
| 卷号 | 171期号:2页码:778-782 |
| 关键词 | proton exchange membrane fuel cell metallic bipolar plate type 304 stainless steel high-energy micro-arc alloying technique TiC coating corrosion pem fuel-cell |
| ISSN号 | 0378-7753 |
| 中文摘要 | Metallic bipolar plates look promising for the replacement of graphite due to higher mechanical strength, better durability to shocks and vibration, no gas permeability, acceptable material cost and superior applicability to mass production. However, the corrosion and passivation of metals in environments of proton exchange membrane fuel cell (PEMFC) cause considerable power degradation. Great attempts were conducted to improve the corrosion resistance of metals while keeping low contact resistance. In this paper, a simple, novel and cost-effective high-energy micro-arc alloying process was employed to prepare compact titanium carbide as coatings for the type 304 stainless steel bipolar plates with a metallurgical bonding between the coating and substrate. It was found that TiC coating increased the corrosion potential of the bare steel in 1 M H2SO4 solution at room temperature by more than 200 mV, and decreased significantly its corrosion current density from 8.3 mu A cm(-2) for the bare steel to 0.034 mu A cm(-2) for the TiC-coated steel. No obvious degradation was observed for the TiC coatings after 30-day exposure in solution. (C) 2007 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33796]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. J. Ren,C. L. Zeng. Corrosion protection of 304 stainless steel bipolar plates using TiC films produced by high-energy micro-arc alloying process[J]. Journal of Power Sources,2007,171(2):778-782. |
| APA | Y. J. Ren,&C. L. Zeng.(2007).Corrosion protection of 304 stainless steel bipolar plates using TiC films produced by high-energy micro-arc alloying process.Journal of Power Sources,171(2),778-782. |
| MLA | Y. J. Ren,et al."Corrosion protection of 304 stainless steel bipolar plates using TiC films produced by high-energy micro-arc alloying process".Journal of Power Sources 171.2(2007):778-782. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。