Low-temperature synthesis/densification and properties Of Si2N2O prepared with Li2O additive
文献类型：期刊论文
| 作者 | Q. F. Tong ; J. Y. Wang ; Z. P. Li ; Y. C. Zhou |
| 刊名 | Journal of the European Ceramic Society
 |
| 出版日期 | 2007 |
| 卷号 | 27期号:16页码:4767-4772 |
| 关键词 | Si2N2O sintering mechanical properties dielectric properties silicon oxynitride ceramics thermal-conductivity nitride densification toughness strength yttria system |
| ISSN号 | 0955-2219 |
| 中文摘要 | Dense Si2N2O was successfully synthesized using 2 mol% Li2O as an additive by a hot-pressing method at 1500 degrees C. Compared to other metal oxide additives, Li2O can significantly decrease the sintering temperature of Si2N2O, which is ascribed to the lower melting point of Li2O-SiO2 and the formation of less viscous liquid phase. Increasing Li2O content has no apparent influence on the mechanical and dielectric properties of dense Si2N2O, which is due to the easy evaporation of Li2O at sintering temperature. The mechanical properties of Si2N2O with Li2O additive are comparable to those of Si2N2O synthesized with other additives. The as-prepared bulk Si2N2O with 2 mol% Li2O additive exhibits both low dielectric constant (6.17 at 1 MHz) and loss tangent (0.0008 at 1 MHz) and combines good mechanical performance, indicating it is a potential high-temperature structural/functional material. (C) 2007 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33840]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Q. F. Tong,J. Y. Wang,Z. P. Li,et al. Low-temperature synthesis/densification and properties Of Si2N2O prepared with Li2O additive[J]. Journal of the European Ceramic Society,2007,27(16):4767-4772. |
| APA | Q. F. Tong,J. Y. Wang,Z. P. Li,&Y. C. Zhou.(2007).Low-temperature synthesis/densification and properties Of Si2N2O prepared with Li2O additive.Journal of the European Ceramic Society,27(16),4767-4772. |
| MLA | Q. F. Tong,et al."Low-temperature synthesis/densification and properties Of Si2N2O prepared with Li2O additive".Journal of the European Ceramic Society 27.16(2007):4767-4772. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。