Characteristics of a SiO2-B2O3-Al2O3-BaCO3-PbO2-ZnO glass-ceramic sealant for SOFCs
文献类型：期刊论文
| 作者 | R. F. Wang ; Z. Lu ; C. Q. Liu ; R. B. Zhu ; X. Q. Huang ; B. Wei ; N. Ai ; W. H. Su |
| 刊名 | Journal of Alloys and Compounds
 |
| 出版日期 | 2007 |
| 卷号 | 432期号:1-2页码:189-193 |
| 关键词 | solid oxide fuel cells glass sealant thermal expansion resistivity contact angle oxide fuel-cells compressive mica seals microscopy mg |
| ISSN号 | 0925-8388 |
| 中文摘要 | A glass system based on SiO2-B2O3-Al2O3-BaCO3-PbO2-ZnO was prepared and a sort of compounding was optimized to determine the composition with best performance named AF8. The technical thermal expansion coefficient (t-TEC) is 10.58 x 10(-6) K-1 between 323 and 773 K. The resistivity of AF8 is 1.95 x 10(4) Omega cm at 800 degrees C. The optimum sealing temperature range was 850-880 degrees C. AF8 glass sealant could adhere with electrolyte of yttria stabilized zirconia (YSZ) well and there were no perforative pores in the sealant. The leak rate of AF8 glass was 0.81 x 10(-7) mbar 1 s(-1) cm(-1) at 800 degrees C tested by oxygen coulometric titration which was closed to the required value. Around the sealing temperature, contact angle of AF8 on YSZ is about 110 degrees. This angle can make them adhere well under a suitable pressure, and also avoids glass spreading freely on surface of the electrolyte. All measured results approved that AF8 may become a practical sealant for SOFCs. (c) 2006 Published by Elsevier B.V. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33871]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | R. F. Wang,Z. Lu,C. Q. Liu,et al. Characteristics of a SiO2-B2O3-Al2O3-BaCO3-PbO2-ZnO glass-ceramic sealant for SOFCs[J]. Journal of Alloys and Compounds,2007,432(1-2):189-193. |
| APA | R. F. Wang.,Z. Lu.,C. Q. Liu.,R. B. Zhu.,X. Q. Huang.,...&W. H. Su.(2007).Characteristics of a SiO2-B2O3-Al2O3-BaCO3-PbO2-ZnO glass-ceramic sealant for SOFCs.Journal of Alloys and Compounds,432(1-2),189-193. |
| MLA | R. F. Wang,et al."Characteristics of a SiO2-B2O3-Al2O3-BaCO3-PbO2-ZnO glass-ceramic sealant for SOFCs".Journal of Alloys and Compounds 432.1-2(2007):189-193. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。