Influence of themal exposure on gamma ' precipitation and tensile properties of DZ951 alloy
文献类型：期刊论文
| 作者 | P. C. Xia ; J. J. Yu ; X. F. Sun ; H. R. Guan ; Z. Q. Hu |
| 刊名 | Materials Characterization
 |
| 出版日期 | 2007 |
| 卷号 | 58期号:7页码:645-651 |
| 关键词 | DZ951 alloy thermal exposure yield stress gamma' phase ni-base superalloy heat-treatment mechanical-properties microstructure gtd-111 alloy |
| ISSN号 | 1044-5803 |
| 中文摘要 | The effect of long-term exposure on the gamma' phase and the tensile behavior of a directionally solidified nickel-base superalloy DZ951 was investigated. Alloys after standard heat treatment (SHT) were isothermally aged at 900 degrees C up to 2000 h and tensile tests were performed in both SHT and aged conditions at various temperatures. The morphology of the gamma' phase changes from cuboid to rafting and the size increases from 300 nm at SHT to 930 nm, and the volume fraction of the gamma' phase decreases from 70% at SHT to 65% during aging at 900 degrees C for 2000 h. The changing trend of yield stress at different test temperatures is similar. The yield stress decreases slightly at 600 degrees C. This arises from few dislocations shearing the gamma' precipitates. There is a peak yield stress value at 760 degrees C, which is attributed to the high strength of the gamma' phase, the homogeneous deformation structure, and dislocation-gamma' precipitate and dislocation-dislocation interactions. The yield stress then decreases rapidly with increased temperature. The low strength of the gamma' phase and gamma' rafting at high temperature contribute to the drop of yield stress. The change of tensile elongation is inverse to that of yield stress. The yield stress continuously decreases with the increase of aging time at 900 degrees C. This arises from the coarsening of gamma' and a decrease in the gamma' volume fraction. (C) 2006 Elsevier Inc. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33933]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | P. C. Xia,J. J. Yu,X. F. Sun,et al. Influence of themal exposure on gamma ' precipitation and tensile properties of DZ951 alloy[J]. Materials Characterization,2007,58(7):645-651. |
| APA | P. C. Xia,J. J. Yu,X. F. Sun,H. R. Guan,&Z. Q. Hu.(2007).Influence of themal exposure on gamma ' precipitation and tensile properties of DZ951 alloy.Materials Characterization,58(7),645-651. |
| MLA | P. C. Xia,et al."Influence of themal exposure on gamma ' precipitation and tensile properties of DZ951 alloy".Materials Characterization 58.7(2007):645-651. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。