Hot corrosion of a novel electrodeposited, Ni-6Cr-7Al nanocomposite under molten (0.9Na,0.1K)(2)SO4 at 900 degrees C
文献类型：期刊论文
| 作者 | X. Yang ; X. Peng ; F. Wang |
| 刊名 | Scripta Materialia
 |
| 出版日期 | 2007 |
| 卷号 | 56期号:10页码:891-894 |
| 关键词 | Ni-Cr-Al nanocomposite electroplating nanocrystalline nanoparticle hot corrosion oxidation resistance cr nanocomposite coatings particles behavior alloys scale films |
| ISSN号 | 1359-6462 |
| 中文摘要 | A novel Ni-6Cr-7Al nanocomposite (in wt.%) was fabricated by co-electrodeposition of Ni with Cr and Al nanoparticles from a nickel sulfate bath. The nanocomposite consisted of nanocrystalline Ni matrix and dispersed nanoparticles of Cr and Al. The nanocomposite, compared with conventionally arc-melted Ni-6Cr-7A1 alloy, exhibited a dramatically increased hot corrosion resistance under molten (0.9Na, 0.1 K)(2)SO4 in air at 900 degrees C, because the unique structure of the nanocomposite favored the rapid formation of external alumina scale. (c) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/33978]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. Yang,X. Peng,F. Wang. Hot corrosion of a novel electrodeposited, Ni-6Cr-7Al nanocomposite under molten (0.9Na,0.1K)(2)SO4 at 900 degrees C[J]. Scripta Materialia,2007,56(10):891-894. |
| APA | X. Yang,X. Peng,&F. Wang.(2007).Hot corrosion of a novel electrodeposited, Ni-6Cr-7Al nanocomposite under molten (0.9Na,0.1K)(2)SO4 at 900 degrees C.Scripta Materialia,56(10),891-894. |
| MLA | X. Yang,et al."Hot corrosion of a novel electrodeposited, Ni-6Cr-7Al nanocomposite under molten (0.9Na,0.1K)(2)SO4 at 900 degrees C".Scripta Materialia 56.10(2007):891-894. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。