Mechanical properties, damage and fracture mechanisms of bulk metallic glass materials
文献类型：期刊论文
| 作者 | Z. F. Zhang ; F. F. Wu ; G. He ; J. Eckert |
| 刊名 | Journal of Materials Science & Technology
 |
| 出版日期 | 2007 |
| 卷号 | 23期号:6页码:747-+ |
| 关键词 | bulk metallic glasses (BMGs) mechanical properties shear fracture failure criterion plastic deformation melting phenomenon supercooled liquid region fatigue-crack-propagation nanostructure-dendrite composite soft-magnetic properties serrated plastic-flow ni amorphous-alloys ti-based composites in-situ formation cu-be alloy high-strength |
| ISSN号 | 1005-0302 |
| 中文摘要 | The deformation, damage, fracture, plasticity and melting phenomenon induced by shear fracture were investigated and summarized for Zr-, Cu-, Ti- and Mg-based bulk metallic glasses (BMGs) and their composites. The shear fracture angles of these BMG materials often display obvious differences under compression and tension, and follow either the Mohr-Coulomb criterion or the unified tensile fracture criterion. The compressive plasticity of the composites is always higher than the tensile plasticity, leading to a significant inconsistency. The enhanced plasticity of BMG composites containing ductile dendrites compared to monolithic glasses strongly depends on the details of the microstructure of the composites. A deformation and damage mechanism of pseudo-plasticity, related to local cracking, is proposed to explain the inconsistency of plastic deformation under tension and compression. Besides, significant melting on the shear fracture surfaces was observed. It is suggested that melting is a common phenomenon in these materials with high strength and high elastic energy, as it is typical for BMGs and their composites failing under shear fracture. The melting mechanism can be explained by a combined effect of a significant temperature rise in the shear bands and the instantaneous release of the large amount of elastic energy stored in the material. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34064]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. F. Zhang,F. F. Wu,G. He,et al. Mechanical properties, damage and fracture mechanisms of bulk metallic glass materials[J]. Journal of Materials Science & Technology,2007,23(6):747-+. |
| APA | Z. F. Zhang,F. F. Wu,G. He,&J. Eckert.(2007).Mechanical properties, damage and fracture mechanisms of bulk metallic glass materials.Journal of Materials Science & Technology,23(6),747-+. |
| MLA | Z. F. Zhang,et al."Mechanical properties, damage and fracture mechanisms of bulk metallic glass materials".Journal of Materials Science & Technology 23.6(2007):747-+. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。