Development of yttria-stabilized zirconia thin films via slurry spin coating for intermediate-to-low temperature solid oxide fuel cells
文献类型：期刊论文
| 作者 | K. F. Chen ; Z. Lu ; N. Ai ; X. Q. Huang ; Y. H. Zhang ; X. S. Xin ; R. B. Zhu ; W. H. Su |
| 刊名 | Journal of Power Sources
 |
| 出版日期 | 2006 |
| 卷号 | 160期号:1页码:436-438 |
| 关键词 | solid oxide fuel cells (SOFCs) slurry spin coating yuria-stabilized zirconia thin film impregnation oxygen airflow fabrication electrolyte membranes cathodes sofcs |
| ISSN号 | 0378-7753 |
| 中文摘要 | Yttria-stabilized zirconia (YSZ) thin films were successfully fabricated on porous NiO-YSZ anode substrates via a slurry spin coating method. With similar to 34-mu m-thick Sm0.2Ce0.80O1.9 (SDC)-impregnated La(0.7)Sr(0.3)Mno(3) (LSM) cathodes, a single cell based on a similar to 9-mu m-thick YSZ film exhibited a good performance at intermediate-to-low temperature. The cell produced an open-circuit voltage (OCV) of similar to 1.08 V, and maximum power densities of similar to 0.42 and similar to 0.70 W cm(-2) at 650 degrees C, while the cathode was exposed to the stationary air and blown with 100 mL min(-1) oxygen airflow, respectively. Enhanced cell performance with oxygen airflow was attributed to the improved cathode performance. By separating the total voltage drop into ohmic and non-ohmic contributions, it could be concluded that the cell performance was primarily determined by the polarization of the electrodes. It is believed that by optimizing the film fabrication process and improving the cathode performance, intermediate-to-low temperature solid oxide fuel cells (SOFCs) based on supported YSZ electrolyte thin films could be put into practice in not far future. (c) 2006 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34145]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | K. F. Chen,Z. Lu,N. Ai,et al. Development of yttria-stabilized zirconia thin films via slurry spin coating for intermediate-to-low temperature solid oxide fuel cells[J]. Journal of Power Sources,2006,160(1):436-438. |
| APA | K. F. Chen.,Z. Lu.,N. Ai.,X. Q. Huang.,Y. H. Zhang.,...&W. H. Su.(2006).Development of yttria-stabilized zirconia thin films via slurry spin coating for intermediate-to-low temperature solid oxide fuel cells.Journal of Power Sources,160(1),436-438. |
| MLA | K. F. Chen,et al."Development of yttria-stabilized zirconia thin films via slurry spin coating for intermediate-to-low temperature solid oxide fuel cells".Journal of Power Sources 160.1(2006):436-438. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。