Microstructure and property of sub-micro WC-10%Co particulate reinforced Cu matrix composites prepared by selective laser sintering
文献类型：期刊论文
| 作者 | D. D. Gu ; Y. F. Shen ; P. Dai ; M. C. Yang |
| 刊名 | Transactions of Nonferrous Metals Society of China
 |
| 出版日期 | 2006 |
| 卷号 | 16期号:2页码:357-362 |
| 关键词 | selective laser sintering metal matrix composites Cu matrix composite WC-Co Cu microstructure microhardness wc-co metal powders densification alloy parts |
| ISSN号 | 1003-6326 |
| 中文摘要 | The WC-10%Co particulate reinforced Cu matrix composite material with a WC-Co : Cu mass ratio of 20 : 80 was successfully fabricated by selective laser sintering(SLS) process. The following optimal processing parameters were used: laser power of 700 W, scan speed of 0.06 m/s, scan line spacing of 0.15 mm, and powder layer thickness of 0.3 mm. The microstructure, composition, and phase of the laser processed material were investigated by scanning electron microscopy(SEM), X-ray diffraction(XRD), and energy dispersive X-ray(EDX) spectroscopy. The results show that the bonding mechanism of this process is liquid phase sintering. The Cu and Co act as the binder phase, while the WC acts as the reinforcing phase. The non-equilibrium effects induced by laser melting, such as high degrees of undercooling and high solidification rate, result in the formation of a metastable phase CoC0.25. The WC reinforcing particulates typically have three kinds of morphology. They are agglomerated and undissolved, incompletely separated and partially dissolved, separated and dissolved, which indicates that particle rearrangement acts as the dominant sintering mechanism for the larger WC, while dissolution-precipitation prevails for the smaller WC particles. Microhardness tester was used to determine the Vickers hardness across the cross-section of the laser sintered sample, with the average value being HV(0.1)268.5. However, the hardness varied considerably, which might be attributed to the WC segregation and the high solidification rate experienced by the molten pool. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34220]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | D. D. Gu,Y. F. Shen,P. Dai,et al. Microstructure and property of sub-micro WC-10%Co particulate reinforced Cu matrix composites prepared by selective laser sintering[J]. Transactions of Nonferrous Metals Society of China,2006,16(2):357-362. |
| APA | D. D. Gu,Y. F. Shen,P. Dai,&M. C. Yang.(2006).Microstructure and property of sub-micro WC-10%Co particulate reinforced Cu matrix composites prepared by selective laser sintering.Transactions of Nonferrous Metals Society of China,16(2),357-362. |
| MLA | D. D. Gu,et al."Microstructure and property of sub-micro WC-10%Co particulate reinforced Cu matrix composites prepared by selective laser sintering".Transactions of Nonferrous Metals Society of China 16.2(2006):357-362. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。