Oxidation and hot corrosion behavior of gradient NiCoCrAlYSiB coatings deposited by a combination of arc ion plating and magnetron sputtering techniques
文献类型：期刊论文
| 作者 | M. H. Guo ; Q. M. Wang ; J. Gong ; C. Sun ; R. F. Huang ; L. S. Wen |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2006 |
| 卷号 | 48期号:9页码:2750-2764 |
| 关键词 | gradient NiCoCrAlYSiB coating arc ion plating hot corrosion oxidation mcraly coatings dislocations resistance diffusion alloy |
| ISSN号 | 0010-938X |
| 中文摘要 | NiCoCrAlYSiB coating was prepared by arc ion plating and Al and Cr gradient NiCoCrAlYSiB coating by a combination of arc ion plating and magnetron sputtering. The results of EPMA show that the Al and Cr are uniformly distributed in the NiCoCrAlYSiB coating but have a graded distribution in the surface layer of the gradient coating. Compared to the bare DSM 11, both the NiCoCrAlYSiB coating and the gradient coating improved the oxidation resistance greatly. After 100 h hot corrosion, the gradient coating showed the best corrosion resistance. The oxidation and hot corrosion mechanisms were discussed. (c) 2005 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34225]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | M. H. Guo,Q. M. Wang,J. Gong,et al. Oxidation and hot corrosion behavior of gradient NiCoCrAlYSiB coatings deposited by a combination of arc ion plating and magnetron sputtering techniques[J]. Corrosion Science,2006,48(9):2750-2764. |
| APA | M. H. Guo,Q. M. Wang,J. Gong,C. Sun,R. F. Huang,&L. S. Wen.(2006).Oxidation and hot corrosion behavior of gradient NiCoCrAlYSiB coatings deposited by a combination of arc ion plating and magnetron sputtering techniques.Corrosion Science,48(9),2750-2764. |
| MLA | M. H. Guo,et al."Oxidation and hot corrosion behavior of gradient NiCoCrAlYSiB coatings deposited by a combination of arc ion plating and magnetron sputtering techniques".Corrosion Science 48.9(2006):2750-2764. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。