Atomic-scale microstructures of Zr(2)Al(3)C(4) and Zr(3)Al(3)C(5) ceramics

文献类型:期刊论文

作者Z. J. Lin ; M. J. Zhuo ; L. F. He ; Y. C. Zhou ; M. S. Li ; J. Y. Wang
刊名Acta Materialia
出版日期2006
卷号54期号:14页码:3843-3851
关键词TEM carbides layered structures STEM transmission electron-microscope mechanical-properties crystal-structure ternary-systems behavior ti3sic2 al carbide ti2alc phases
ISSN号1359-6454
中文摘要The microstructures of bulk Zr(2)Al(3)C(4) and Zr(3)Al(3)C(5) ceramics have been investigated using transmission electron microscopy and scanning transmission electron microscopy. These two carbides were determined to have a point group 6/mmm and a space group P6(3)/mmc using selected-area electron diffraction and convergent beam electron diffraction. The atomic-scale microstructures of Zr(2)Al(3)C(4) and Zr(3)Al(3)C(5) were investigated through high-resolution imaging and Z-contrast imaging. Furthermore, intergrowth between Zr(2)Al(3)C(4) and Zr(3)Al(3)C(5) was identified. Stacking faults in Zr(3)Al(3)C(5) were found to result from the insertion of an additional Zr-C layer. Cubic ZrC was occasionally identified to be incorporated in elongated Zr3Al3C5 grains. In addition, Al may induce a twinned ZrC structure and lead to the formation of ternary zirconium aluminum carbides. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
原文出处://WOS:000240171400021
公开日期2012-04-13
源URL[http://ir.imr.ac.cn/handle/321006/34332]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
Z. J. Lin,M. J. Zhuo,L. F. He,et al. Atomic-scale microstructures of Zr(2)Al(3)C(4) and Zr(3)Al(3)C(5) ceramics[J]. Acta Materialia,2006,54(14):3843-3851.
APA Z. J. Lin,M. J. Zhuo,L. F. He,Y. C. Zhou,M. S. Li,&J. Y. Wang.(2006).Atomic-scale microstructures of Zr(2)Al(3)C(4) and Zr(3)Al(3)C(5) ceramics.Acta Materialia,54(14),3843-3851.
MLA Z. J. Lin,et al."Atomic-scale microstructures of Zr(2)Al(3)C(4) and Zr(3)Al(3)C(5) ceramics".Acta Materialia 54.14(2006):3843-3851.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。