The corrosion behavior of Fe-10Cr nanocrystalline coating

文献类型:期刊论文

作者G. Z. Meng ; Y. Li ; F. H. Wang
刊名Electrochimica Acta
出版日期2006
卷号51期号:20页码:4277-4284
关键词nanocystalline grain size corrosion behavior passive film impedance plane displays stainless-steel passive films stability conditions steady-state oxidation alloys
ISSN号0013-4686
中文摘要Fe-10Cr nanocrystalline (nc) coatings with a grain size of 20-30 nm were synthesized on glass substrates by magnetron sputtering. The corrosion behavior was investigated in 0.05 mol/L H2SO4 + 0.25 mol/L Na2SO4 and 0.05 mol/L H2SO4 + 0.5 mol/L NaCl solution by polarization curves, EIS and Mott-Schottky analysis. The results showed that compared to Fe-10Cr cast alloy, the active dissolution of the coating was accelerated; the passive film contained more Cr and therefore the coating was easier to passivate. The passive films formed on Fe-10Cr nc and cast alloy exhibited n-type semiconducting behavior in acidic solutions without Cl- and p-type semiconducting behavior in acidic solutions with Cl-. The lower breakdown potential for both materials in the solution with Cl- is related to the p-type passive film formed on them. For Fe-10Cr nc, lower donor density and increased Cr content were responsible for the chemical stability of the passive film. (c) 2005 Published by Elsevier Ltd.
原文出处://WOS:000238111000023
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/34406]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
G. Z. Meng,Y. Li,F. H. Wang. The corrosion behavior of Fe-10Cr nanocrystalline coating[J]. Electrochimica Acta,2006,51(20):4277-4284.
APA G. Z. Meng,Y. Li,&F. H. Wang.(2006).The corrosion behavior of Fe-10Cr nanocrystalline coating.Electrochimica Acta,51(20),4277-4284.
MLA G. Z. Meng,et al."The corrosion behavior of Fe-10Cr nanocrystalline coating".Electrochimica Acta 51.20(2006):4277-4284.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。