Electrochemical corrosion performance in 3.5% NaCl of the electrodeposited nanocrystalline Ni films with and without dispersions of Cr nanoparticles
文献类型：期刊论文
| 作者 | X. Peng ; Y. Zhang ; J. Zhao ; F. Wang |
| 刊名 | Electrochimica Acta
 |
| 出版日期 | 2006 |
| 卷号 | 51期号:23页码:4922-4927 |
| 关键词 | electrodeposition electrochemical corrosion nanocrystalline Ni film Cr nanoparticles X-ray photoelectron spectroscopy localized corrosion nanocomposite film pitting corrosion grain-size behavior nickel alloys oxidation resistance passivity |
| ISSN号 | 0013-4686 |
| 中文摘要 | Nanocrystalline (nc) Ni films with and without dispersions of Cr nanoparticles were electrodeposited from a nickel sulfate bath. The grain size of the nc-Ni films was reduced with increasing in the co-deposition content of Cr nanoparticles. Potentiodynamic polarization tests showed that increasing in the co-deposition content resulted in an enlarged passive region of the nc-Ni in 3.5% NaCl through reducing the corrosion potential and increasing the breakdown potential. Scanning electron microscopy (SEM) observation indicated that the polarized pure nc-Ni film exhibited numerous large and deep pits. However, they became smaller and shallower when 4.5 wt.% Cr nanoparticles were co-deposited, and almost disappeared when 10.9 wt.% Cr were co-deposited. X-ray photoelectron spectroscopy (XPS) analysis showed that the different electrochemical corrosion performance was associated with the ability of the Cr nanoparticles co-deposited nc-Ni film to form a continuous Cr-oxide passive film. (c) 2006 Published by Elsevier Ltd. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34426]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. Peng,Y. Zhang,J. Zhao,et al. Electrochemical corrosion performance in 3.5% NaCl of the electrodeposited nanocrystalline Ni films with and without dispersions of Cr nanoparticles[J]. Electrochimica Acta,2006,51(23):4922-4927. |
| APA | X. Peng,Y. Zhang,J. Zhao,&F. Wang.(2006).Electrochemical corrosion performance in 3.5% NaCl of the electrodeposited nanocrystalline Ni films with and without dispersions of Cr nanoparticles.Electrochimica Acta,51(23),4922-4927. |
| MLA | X. Peng,et al."Electrochemical corrosion performance in 3.5% NaCl of the electrodeposited nanocrystalline Ni films with and without dispersions of Cr nanoparticles".Electrochimica Acta 51.23(2006):4922-4927. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。