Structural and magnetic properties of Laves compounds Dy1-xPrx(Fe0.35Co0.55B0.1)(2) (0 <= x <= 1)
文献类型：期刊论文
| 作者 | W. J. Ren ; D. Li ; Y. C. Sui ; W. Liu ; X. G. Zhao ; J. J. Liu ; J. Li ; Z. D. Zhang |
| 刊名 | Journal of Applied Physics
 |
| 出版日期 | 2006 |
| 卷号 | 99期号:8 |
| 关键词 | spontaneous magnetostriction alloys prfe2 boron |
| ISSN号 | 0021-8979 |
| 中文摘要 | Dy1-xPrx(Fe0.35Co0.55B0.1)(2) (0 <= x <= 1) Laves compounds with a cubic MgCu2-type structure were synthesized by arc melting and subsequent annealing. The lattice parameter of the Laves compounds linearly increases, while the Curie temperature T-C decreases with increasing Pr content. The saturation magnetization M-s at 5 K or 295 K for the Dy1-xPrx(Fe0.35Co0.55B0.1)(2) alloys decreases to reach a minimum, then increases with increasing Pr content. The composition for magnetic moment compensation is about x=0.55 at 295 K and x=0.65 at 5 K, respectively. The magnetostriction lambda(parallel to) or lambda(perpendicular to) at room temperature was investigated either parallel or perpendicular to the applied field using a standard strain gauge technique. (C) 2006 American Institute of Physics. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34445]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | W. J. Ren,D. Li,Y. C. Sui,et al. Structural and magnetic properties of Laves compounds Dy1-xPrx(Fe0.35Co0.55B0.1)(2) (0 <= x <= 1)[J]. Journal of Applied Physics,2006,99(8). |
| APA | W. J. Ren.,D. Li.,Y. C. Sui.,W. Liu.,X. G. Zhao.,...&Z. D. Zhang.(2006).Structural and magnetic properties of Laves compounds Dy1-xPrx(Fe0.35Co0.55B0.1)(2) (0 <= x <= 1).Journal of Applied Physics,99(8). |
| MLA | W. J. Ren,et al."Structural and magnetic properties of Laves compounds Dy1-xPrx(Fe0.35Co0.55B0.1)(2) (0 <= x <= 1)".Journal of Applied Physics 99.8(2006). |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。