Electroplating zinc transition layer for electroless nickel plating on AM60 magnesium alloys
文献类型：期刊论文
| 作者 | X. M. Wang ; W. Q. Zhou ; E. H. Han |
| 刊名 | Transactions of Nonferrous Metals Society of China
 |
| 出版日期 | 2006 |
| 卷号 | 16页码:S1798-S1801 |
| 关键词 | magnesium alloy AM60 electroplating zinc electroless nickel plating corrosion resistance |
| ISSN号 | 1003-6326 |
| 中文摘要 | Electroplating zinc coating as transition layer of electroless nickel plating on AM60 magnesium alloys was investigated. The zinc film can be deposited in a pyrophosphate bath at 50-60 degrees C under current density of 0.5-1.5 A/dm(2). A new fore treatment technology was applied by acid cleaning with a solution containing molybdate and phosphorous acid, by alkaline cleaning in a bath containing molybdate and sodium hydroxide. The subsequent electroless plating was carried out in nickel sulfate bath. The SEM observation shows that the deposition is uniform and compact. The polarization curve measurements show that the corrosion potential of the zinc plating in 3.5% NaCl is about -1.3 V(vs SCE) which is noble than that of magnesium substrate. The zinc electroplating can be applied as the pretreatment process for electroless nickel plating on magnesium alloys. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34533]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. M. Wang,W. Q. Zhou,E. H. Han. Electroplating zinc transition layer for electroless nickel plating on AM60 magnesium alloys[J]. Transactions of Nonferrous Metals Society of China,2006,16:S1798-S1801. |
| APA | X. M. Wang,W. Q. Zhou,&E. H. Han.(2006).Electroplating zinc transition layer for electroless nickel plating on AM60 magnesium alloys.Transactions of Nonferrous Metals Society of China,16,S1798-S1801. |
| MLA | X. M. Wang,et al."Electroplating zinc transition layer for electroless nickel plating on AM60 magnesium alloys".Transactions of Nonferrous Metals Society of China 16(2006):S1798-S1801. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。