Wear and corrosion properties of a low carbon steel processed by means of SMAT followed by lower temperature chromizing treatment
文献类型：期刊论文
| 作者 | Z. B. Wang ; J. Lu ; K. Lu |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2006 |
| 卷号 | 201期号:6页码:2796-2801 |
| 关键词 | low carbon steel surface mechanical attrition treatment lower temperature chromizing wear resistance corrosion resistance mechanical attrition treatment surface nanocrystallization alloy resistance diffusion iron |
| ISSN号 | 0257-8972 |
| 中文摘要 | A duplex lower temperature chromizing treatment at 600 degrees C for 120 min followed by 860 degrees C for 90 min was performed on a low carbon steel plate with a nanostructured surface layer, induced by surface mechanical attrition treatment (SMAT) [Z.B. Wang, J. Lu, K. Lu, Acta Mater. 53 (2005) 2081]. Microhardness, wear and corrosion resistances of the chromized SMAT sample were measured, in comparison with those of the chromized coarse-grained counterpart and the as-annealed coarse-grained sample. Experimental results showed that these properties were improved markedly. The much enhanced properties of the chromized SMAT sample relative to the chromized coarse-grained counterpart might originate from its superior microstructures, i.e., a much thicker chromized surface layer with smaller grains and more homogenous phase-distribution, due to the employed processes of the SMAT and the duplex lower temperature chromizing treatment. (c) 2006 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34543]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. B. Wang,J. Lu,K. Lu. Wear and corrosion properties of a low carbon steel processed by means of SMAT followed by lower temperature chromizing treatment[J]. Surface & Coatings Technology,2006,201(6):2796-2801. |
| APA | Z. B. Wang,J. Lu,&K. Lu.(2006).Wear and corrosion properties of a low carbon steel processed by means of SMAT followed by lower temperature chromizing treatment.Surface & Coatings Technology,201(6),2796-2801. |
| MLA | Z. B. Wang,et al."Wear and corrosion properties of a low carbon steel processed by means of SMAT followed by lower temperature chromizing treatment".Surface & Coatings Technology 201.6(2006):2796-2801. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。