Influence of surface finish on fatigue cracking behavior of reactor pressure vessel steel in high temperature water
文献类型：期刊论文
| 作者 | X. Q. Wu ; H. Guan ; E. H. Han ; W. Ke ; Y. Katada |
| 刊名 | Materials and Corrosion-Werkstoffe Und Korrosion
 |
| 出版日期 | 2006 |
| 卷号 | 57期号:11页码:868-871 |
| 关键词 | environmentally assisted cracking low-cycle fatigue low-alloy corrosion-fatigue growth-behavior carbon |
| ISSN号 | 0947-5117 |
| 中文摘要 | The low cycle fatigue behavior of a low-alloy reactor pressure vessel (RPV) steel was investigated in high temperature water. Main attention was paid to the effects of surface finish of specimens on fatigue cracking behavior. It was found that the influence of surface finish on fatigue resistance of the steel was strain-rate dependent in high temperature water. Pretty obvious degradation of fatigue resistance appeared at fast strain rate with rougher surface finish. At slow strain rate, surface circumferential scratches promoted crack initiation and propagation. The fracture surface showed relatively flat and slight crack-arrest features. At fast strain rate, surface scratches also promoted crack initiation, but seemed not to dominate crack propagation. The fracture surface showed typical terraced and fan-like features. The above fatigue cracking behavior can be rationalized by a strain-rate dependent environmentally assisted cracking process of low-alloy RPV steel in high temperature water. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34583]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. Q. Wu,H. Guan,E. H. Han,et al. Influence of surface finish on fatigue cracking behavior of reactor pressure vessel steel in high temperature water[J]. Materials and Corrosion-Werkstoffe Und Korrosion,2006,57(11):868-871. |
| APA | X. Q. Wu,H. Guan,E. H. Han,W. Ke,&Y. Katada.(2006).Influence of surface finish on fatigue cracking behavior of reactor pressure vessel steel in high temperature water.Materials and Corrosion-Werkstoffe Und Korrosion,57(11),868-871. |
| MLA | X. Q. Wu,et al."Influence of surface finish on fatigue cracking behavior of reactor pressure vessel steel in high temperature water".Materials and Corrosion-Werkstoffe Und Korrosion 57.11(2006):868-871. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。