Glass formation in the ternary Zr-Zr(2)Cu-Zr(2)Ni system
文献类型：期刊论文
| 作者 | H. Yang ; J. Q. Wang ; Y. Li |
| 刊名 | Journal of Non-Crystalline Solids
 |
| 出版日期 | 2006 |
| 卷号 | 352期号:8页码:832-836 |
| 关键词 | amorphous metals metallic glasses transition metals glass formation thermal properties calorimetry glass transition X-ray diffraction zr metallic glasses crystallization characteristics forming ability alloy diameter mm |
| ISSN号 | 0022-3093 |
| 中文摘要 | Glass formation and glass forming ability in the ternary Zr-Cu-Ni system were studied systematically. For Cu mold casting, the critical size for glass formation was found to be 1 mm in a relatively wide composition range of 56-64 at.% Zr, 16-26 at.% 3Cu and 16-24 at.% Ni. The phases competing with glass formation were found to be Zr, Zr(2)Cu and Zr(2)Ni. Despite the fact that Cu and Ni are completely miscible with each other, they cannot be regarded as simple substitution to each other in the case of glass formation in the Zr-Zr(2)Cu-Zr(2)Ni ternary eutectic system. (c) 2006 Published by Elsevier B.V. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34638]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | H. Yang,J. Q. Wang,Y. Li. Glass formation in the ternary Zr-Zr(2)Cu-Zr(2)Ni system[J]. Journal of Non-Crystalline Solids,2006,352(8):832-836. |
| APA | H. Yang,J. Q. Wang,&Y. Li.(2006).Glass formation in the ternary Zr-Zr(2)Cu-Zr(2)Ni system.Journal of Non-Crystalline Solids,352(8),832-836. |
| MLA | H. Yang,et al."Glass formation in the ternary Zr-Zr(2)Cu-Zr(2)Ni system".Journal of Non-Crystalline Solids 352.8(2006):832-836. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。