Effect of nanocrystallization on sulfur segregation in Fe-Cr-Al alloy during oxidation at 1000 degrees C
文献类型：期刊论文
| 作者 | S. L. Yang ; F. H. Wang |
| 刊名 | Oxidation of Metals
 |
| 出版日期 | 2006 |
| 卷号 | 65期号:3-4页码:195-205 |
| 关键词 | nanocrystallization oxidation scale adhesion sulfur segregation high-temperature oxidation oxide scale adherence selective oxidation reactive elements al2o3 scales behavior adhesion resistance impurity growth |
| ISSN号 | 0030-770X |
| 中文摘要 | From the 1980's a theory named "the sulfur effect" has been applied to explain the scale adhesion and the reactive-element effect (REE) during high-temperature oxidation. It claims that the bond between the oxide scale and the metal substrate is intrinsically strong and that impurity sulfur in the metal segregates at the oxide scale/substrate interface and weakens the bond, and that REs getter the sulfur impurity and prevent it from segregating to the interface. In the present study, a cast polycrystalline sulfur-containing Fe-25Cr-5Al-1S (wt.%) alloy and its magnetron-sputtered nanocrystalline coating were oxidized at 1000 degrees C, and the specimens were examined by XRD and SEM. The scale formed on the cast alloy was cracked and detached from the substrate even after isothermal exposure, and obvious sulfur enrichment was detectable at the scale/substrate interface. While, the scale formed on the nanocrystalline coating was very adherent after 100 cycles oxidation. Here, sulfur was preferentially distributed in the outer scale and internal oxides rather than at the scale/substrate interface. These results provide evidence that nanocrystallization can prevent sulfur segregation at the scale/substrate interface, hence enhance scale adhesion. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34646]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | S. L. Yang,F. H. Wang. Effect of nanocrystallization on sulfur segregation in Fe-Cr-Al alloy during oxidation at 1000 degrees C[J]. Oxidation of Metals,2006,65(3-4):195-205. |
| APA | S. L. Yang,&F. H. Wang.(2006).Effect of nanocrystallization on sulfur segregation in Fe-Cr-Al alloy during oxidation at 1000 degrees C.Oxidation of Metals,65(3-4),195-205. |
| MLA | S. L. Yang,et al."Effect of nanocrystallization on sulfur segregation in Fe-Cr-Al alloy during oxidation at 1000 degrees C".Oxidation of Metals 65.3-4(2006):195-205. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。