Microstructure and mechanical strength of diffusion-bonded Ti3SiC2/Ni joints
文献类型：期刊论文
| 作者 | X. H. Yin ; M. S. Li ; Y. C. Zhou |
| 刊名 | Journal of Materials Research
 |
| 出版日期 | 2006 |
| 卷号 | 21期号:9页码:2415-2421 |
| 关键词 | silicon-carbide bulk ceramics temperature alloy alumina metals copper nickel phase zr |
| ISSN号 | 0884-2914 |
| 中文摘要 | Diffusion bonding of Ti3SiC2 and nickel has been conducted at temperatures of 800 degrees C-1100 degrees C for 10-90 min under 6-20 MPa in a vacuum. The phase composition and microstructure of the joints were investigated by x-ray diffraction, scanning electron microscopy, and electron probe microanalysis. The total diffusion path of the joining is determined to be Ni/Ni31Si12 + Ni16Ti6Si7 + TiCx/Ti3SiC2 + Ti2Ni + TiCx/Ti3SiC2. The growth of the reaction layer follows parabolic law, and the temperature dependence of the reaction constant, k, can be expressed as k = 1.68 x 10(-4) exp(-118 +/- 12 kJ/RT) m/s(1/2). The diffusion of nickel through the reaction zone toward Ti3SiC2 is the main controlling step in the bonding process. Joint strengths were determined through shear tests. The maximum shear strength of 121 +/- 7 MPa, which is close to the shear strength of Ti3SiC2, has been obtained under the condition of 1000 degrees C for 10 min under 20 MPa. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34667]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. H. Yin,M. S. Li,Y. C. Zhou. Microstructure and mechanical strength of diffusion-bonded Ti3SiC2/Ni joints[J]. Journal of Materials Research,2006,21(9):2415-2421. |
| APA | X. H. Yin,M. S. Li,&Y. C. Zhou.(2006).Microstructure and mechanical strength of diffusion-bonded Ti3SiC2/Ni joints.Journal of Materials Research,21(9),2415-2421. |
| MLA | X. H. Yin,et al."Microstructure and mechanical strength of diffusion-bonded Ti3SiC2/Ni joints".Journal of Materials Research 21.9(2006):2415-2421. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。