Friction and wear behaviors of nanocrystalline surface layer of pure copper

文献类型:期刊论文

作者Y. S. Zhang ; Z. Han ; K. Wang ; K. Lu
刊名Wear
出版日期2006
卷号260期号:9-10页码:942-948
关键词nanocrystalline metals friction and wear copper surface mechnical attrition treatment (SMAT) mechanical attrition treatment sliding behavior grain-size composites steel
ISSN号0043-1648
中文摘要Surface mechanical attrition treatment (SMAT) was employed to fabricate a nanocrystalline surface layer on a pure copper plate. The grain size is about 10 run in the top layer and increases with an increasing depth from the treated surface. The tribological behavior of the nanocrystalline surface layer was investigated under dry conditions. Experimental results show that the load-bearing ability is markedly enhanced with the nanocrystalline surface layer relative to the coarse-grained form. The friction coefficient of the nanocrystalline layer is lower than that of the coarse-grained copper when the applied load is below 20 N. With increase of the load, the difference in wear resistance between the SMAT and the conventional Cu decreases. When the load exceeds 40 N, for the SMAT Cu, there occurs a transition of wear regime from local damage to delamination of a mechanical mixed layer. There is an abrupt increase of the wear volume, which corresponds to the wearing away of the nanocrystalline layer. The enhanced wear properties of the nanocrystalline surface layer are correlated with the stability of the mechanical mixed layer and the high hardness of the nanocrystalline structure. (c) 2005 Elsevier B.V All rights reserved.
原文出处://WOS:000237818600003
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/34726]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
Y. S. Zhang,Z. Han,K. Wang,et al. Friction and wear behaviors of nanocrystalline surface layer of pure copper[J]. Wear,2006,260(9-10):942-948.
APA Y. S. Zhang,Z. Han,K. Wang,&K. Lu.(2006).Friction and wear behaviors of nanocrystalline surface layer of pure copper.Wear,260(9-10),942-948.
MLA Y. S. Zhang,et al."Friction and wear behaviors of nanocrystalline surface layer of pure copper".Wear 260.9-10(2006):942-948.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。