文献类型:期刊论文

作者X. H. Chen ; J. Lu ; L. Lu ; K. Lu
刊名Scripta Materialia
出版日期2005
卷号52期号:10页码:1039-1044
关键词nanocrystalline materials surface mechanical attrition treatment tensile properties 316L austenitic stainless steel mechanical attrition treatment hall-petch relationship surface nanocrystallization iron
ISSN号1359-6462
中文摘要A nanocrystalline 316L austenitic stainless steel sample (mean grain size similar to 40 nm) was prepared by means of surface mechanical attrition treatment. Uniaxial tensile tests at room temperature showed the nanocrystalline sample exhibits an extremely high yield strength up to 1450 MPa, which still follows the Hall-Petch relation extrapolated from the coarse-grained material. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
原文出处://WOS:000227851100017
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/34815]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
X. H. Chen,J. Lu,L. Lu,et al. Tensile properties of a nanocrystalline 316L austenitic stainless steel[J]. Scripta Materialia,2005,52(10):1039-1044.
APA X. H. Chen,J. Lu,L. Lu,&K. Lu.(2005).Tensile properties of a nanocrystalline 316L austenitic stainless steel.Scripta Materialia,52(10),1039-1044.
MLA X. H. Chen,et al."Tensile properties of a nanocrystalline 316L austenitic stainless steel".Scripta Materialia 52.10(2005):1039-1044.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。