Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel
文献类型：期刊论文
| 作者 | Y. He ; K. Yang ; W. Sha |
| 刊名 | Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science
 |
| 出版日期 | 2005 |
| 卷号 | 36A期号:9页码:2273-2287 |
| 关键词 | precipitation reactions phase chemistry transformation plasticity fracture-toughness reverted austenite aging behavior ni alloys mo |
| ISSN号 | 1073-5623 |
| 中文摘要 | The precipitation kinetics in the aging temperature range of 713 to 813 K in a 2000 MPa grade Co-free maraging steel (Fe-18.9 pct Ni-4.1 pet Mo-1.9 pet Ti, mass pct) has been studied. Study on microstructure and mechanical properties showed that a great deal of Ni3Ti and a type of unknown spheroidal precipitates both with average diameter of 2 to 3 nm are formed in the early aging stage at 713 K, which results in a high strength and a relatively low fracture toughness. Ni3Ti precipitates grow into needle or rod shape and become the main precipitation as the aging time is prolonged. Strength increases and fracture toughness (K-1C) decreases with growth of the precipitates. The ultra-high strength of the maraging steel subjected to long-time aging at 713 K is attributed to the high resistance to coarsening of the precipitates. The strengthening in the underaged condition at 713 K is a combination of dislocations cutting through precipitates and the Orowan mechanisms. Aged at 813 K, the size of Ni3Ti precipitates is seriously nonuniform at the early stage and a small amount of interlath reverted austenite is formed. Thereafter, Ni3Ti precipitates coarsen sharply accompanied with the embrittlement. Intralath reverted austenite appears subsequently. In the later stage of aging, the coarsened Ni3Ti precipitates dissolve into the striplike intralath reverted austenite that is disorderly embedded in the matrix. All of these result in a low strength and low fracture toughness under overaging condition. Analysis shows that the formation of reverted austenite contains the diffusion and Kudjumov-Sachs (K-S) and Nishiyama-Wassermann (N-W) shear mechanisms. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34871]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. He,K. Yang,W. Sha. Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel[J]. Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,2005,36A(9):2273-2287. |
| APA | Y. He,K. Yang,&W. Sha.(2005).Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel.Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,36A(9),2273-2287. |
| MLA | Y. He,et al."Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel".Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science 36A.9(2005):2273-2287. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。