Single crystal T(0.3)MoO(3) growth by electrolytic reduction method of a T1(2)CO(3)-MoO(3) melts
文献类型：期刊论文
| 作者 | C. Z. Li ; R. Xiong ; D. Yin ; Z. Tang ; J. F. Wang ; D. H. Li ; Z. X. Yu ; J. Shi |
| 刊名 | Journal of Crystal Growth
 |
| 出版日期 | 2005 |
| 卷号 | 285期号:1-2页码:81-87 |
| 关键词 | electrolytic reduction single crystal growth thallium blue bronze Tl(0).(3)MoO(3) charge density wave charge-density-wave molybdenum oxide bronzes blue bronze nonlinear transport k0.3moo3 k0.30moo3 memory dynamics lithium noise |
| ISSN号 | 0022-0248 |
| 中文摘要 | Single crystals of quasi-one-dimensional charge-density-wave conductor blue bronze Tl(0.3)MoO(3) have been grown by electrolytic reduction method using the raw materials Tl(2)CO(3)-MoO(3) with composition around 1:4.3 mol ration. The electrolytic temperature was about 570 degrees C, and electrolytic current was 25 mA during the electrolytic process. By this method, the Tl(0.3)MoO(3) single crystals obtained have a relatively large average size and high quality. Platelet crystals with typical dimensions of 7 x 2 x 1 mm(3) were obtained. The crystal structure is monoclinic with space group C2/m. The parameters of the unit cell of the single crystal are as follows: a = 18.486(6)angstrom, b = 7.555(2)angstrom, c = 10.032(3)angstrom and beta = 118.38(3)degrees. The C-center symmetry of Tl(0.3)MoO(3) crystal is demonstrated by the selected area electron diffraction (SAED) patterns in the transmission electron microscope (TEM). The full-width at half-maximum (FWHM) of the rocking curve of the (201) Bragg peak of the Tl(0.3)MoO(3) was approximately 0.4 degrees. These are evidences that the single crystal is of high quality. The temperature dependence of the resistivity shows that a metal-semiconductor transition occurs near 181 K. (c) 2005 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34895]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | C. Z. Li,R. Xiong,D. Yin,et al. Single crystal T(0.3)MoO(3) growth by electrolytic reduction method of a T1(2)CO(3)-MoO(3) melts[J]. Journal of Crystal Growth,2005,285(1-2):81-87. |
| APA | C. Z. Li.,R. Xiong.,D. Yin.,Z. Tang.,J. F. Wang.,...&J. Shi.(2005).Single crystal T(0.3)MoO(3) growth by electrolytic reduction method of a T1(2)CO(3)-MoO(3) melts.Journal of Crystal Growth,285(1-2),81-87. |
| MLA | C. Z. Li,et al."Single crystal T(0.3)MoO(3) growth by electrolytic reduction method of a T1(2)CO(3)-MoO(3) melts".Journal of Crystal Growth 285.1-2(2005):81-87. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。