Phase transformation during aging and resulting mechanical properties of two Ti-Nb-Ta-Zr alloys
文献类型：期刊论文
| 作者 | S. J. Li ; R. Yang ; M. Niinomi ; Y. L. Hao ; Y. Y. Cui ; Z. X. Gu |
| 刊名 | Materials Science and Technology
 |
| 出版日期 | 2005 |
| 卷号 | 21期号:6页码:678-686 |
| 关键词 | metastable beta titanium alloy phase transformation Young's modulus mechanical properties youngs modulus omega-phase biomedical applications titanium-alloys cast-iron ti-29nb-13ta-4.6zr competition martensite ti-6al-4v beta |
| ISSN号 | 0267-0836 |
| 中文摘要 | Phase transformations and mechanical properties of both Ti-29Nb-13Ta-4 center dot 6Zr and Ti-39Nb-13Ta-4 center dot 6Zr (wt-%) alloys were investigated. The microstructure of the 29Nb alloy is sensitive to solution and aging treatment. Ice water quenching from the solution treatment temperature resulted in (beta+alpha '') microstructure but air or furnace cooling led to a mixture of (beta+omega). The formation of the orthorhombic alpha '' martensite thus suppresses omega formation in the ice water quenched 29Nb alloy. Cooling rate from the solution treatment temperature also has a significant effect on the formation of alpha and omega phases during subsequent isothermal aging below the omega start temperature: slow cooling enhances omega but depresses alpha formation. This cooling rate dependence of aged microstructure was attributed to alpha '' martensite acting as precursor of the alpha phase, thus providing a low energy path to the precipitation of alpha at the expense of omega. Phase transformation in the 39Nb alloy is more sluggish than that in the 29Nb alloy, owing to the presence of the higher content of beta stabiliser Nb. For the 29Nb alloy, Young's modulus and mechanical properties are sensitive to the fraction of phases, and change significantly during aging, in contrast with the 39Nb alloy. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34904]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | S. J. Li,R. Yang,M. Niinomi,et al. Phase transformation during aging and resulting mechanical properties of two Ti-Nb-Ta-Zr alloys[J]. Materials Science and Technology,2005,21(6):678-686. |
| APA | S. J. Li,R. Yang,M. Niinomi,Y. L. Hao,Y. Y. Cui,&Z. X. Gu.(2005).Phase transformation during aging and resulting mechanical properties of two Ti-Nb-Ta-Zr alloys.Materials Science and Technology,21(6),678-686. |
| MLA | S. J. Li,et al."Phase transformation during aging and resulting mechanical properties of two Ti-Nb-Ta-Zr alloys".Materials Science and Technology 21.6(2005):678-686. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。