Interfacial shear strength measurements of SiC fiber-reinforced titanium composites
文献类型：期刊论文
| 作者 | Y. H. Li ; N. L. Shi ; D. Z. Zhang ; R. Yang |
| 刊名 | Journal of Materials Science & Technology
 |
| 出版日期 | 2005 |
| 卷号 | 21期号:5页码:657-660 |
| 关键词 | push-out test SiCf / Ti composites powder coated fiber interfacial shear strength matrix composites |
| ISSN号 | 1005-0302 |
| 中文摘要 | A continuous loading push-out test technique was used to measure the interfacial shear strength of SiC fiber reinforced Ti matrix composites. The interfacial shear strength of samples as-fabricated and after heat exposed at 700 and 800 degrees C for 50 h was successfully determined. It has been found that the interfacial shear strength of the specimen exposed at 700 degrees C was higher than that of as-prepared and exposed samples at 8000C. The shear strength of the as-prepared samples was about 112.45 MPa, and increased to about 153.77 MPa after heat-treating at 700 degrees C for 50 h, but decreased to 133.11 MPa after treating at 800 degrees C for 50 h. Scanning electron microscope (SEM) was used to investigate the interfacial morphology of the samples. The brittle phase was the main products of interface for samples exposed at 800 degrees C, and the interface was easily peeled off. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34916]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. H. Li,N. L. Shi,D. Z. Zhang,et al. Interfacial shear strength measurements of SiC fiber-reinforced titanium composites[J]. Journal of Materials Science & Technology,2005,21(5):657-660. |
| APA | Y. H. Li,N. L. Shi,D. Z. Zhang,&R. Yang.(2005).Interfacial shear strength measurements of SiC fiber-reinforced titanium composites.Journal of Materials Science & Technology,21(5),657-660. |
| MLA | Y. H. Li,et al."Interfacial shear strength measurements of SiC fiber-reinforced titanium composites".Journal of Materials Science & Technology 21.5(2005):657-660. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。