Corrosion electrochemical behavior of brass tubes in circulating cooling seawater
文献类型：期刊论文
| 作者 | Y. Z. Lu ; S. Z. Song ; L. H. Yin |
| 刊名 | Transactions of Nonferrous Metals Society of China
 |
| 出版日期 | 2005 |
| 卷号 | 15期号:3页码:619-625 |
| 关键词 | brass tube seawater electrochemical impedance spectroscopy electrochemical noise noise data transform eis |
| ISSN号 | 1003-6326 |
| 中文摘要 | electrochemical behavior of brass tubes in circulating cooling seawater using the developed sensor. EIS study shows that the inhibitor can lead to the formation of corrosion products on metal surface, which will then inhibit the corrosion process. When the flow rate of the seawater increases, the diffusion of oxygen speeds up and the action of filming on HA177-2 tube accelerates, resulting in decrease of corrosion rate. EN analysis shows that the flow rate of the seawater has little effect on pitting susceptivity of HSn70-1 tube; however the pitting susceptivity of HA177-2 tube increases with increasing flow rate. Good agreement is observed between the spectral noise resistance R-sn (f) calculated from EN data and the modulus of impedance. It is shown that the electrochemical noise technique can be used in corrosion monitoring. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/34965]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. Z. Lu,S. Z. Song,L. H. Yin. Corrosion electrochemical behavior of brass tubes in circulating cooling seawater[J]. Transactions of Nonferrous Metals Society of China,2005,15(3):619-625. |
| APA | Y. Z. Lu,S. Z. Song,&L. H. Yin.(2005).Corrosion electrochemical behavior of brass tubes in circulating cooling seawater.Transactions of Nonferrous Metals Society of China,15(3),619-625. |
| MLA | Y. Z. Lu,et al."Corrosion electrochemical behavior of brass tubes in circulating cooling seawater".Transactions of Nonferrous Metals Society of China 15.3(2005):619-625. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。