Pretreatment effect on the synthesis of Ag-coated Al(2)O(3) powders by electroless deposition process
文献类型：期刊论文
| 作者 | G. M. Shi ; J. K. Han ; Z. D. Zhang ; H. Y. Song ; B. T. Lee |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2005 |
| 卷号 | 195期号:2-3页码:333-337 |
| 关键词 | silver electroless deposition nanocoating Al(2)O(3) powder TEM microstructure fabrication nanocomposites toughness ceramics behavior copper phase |
| ISSN号 | 0257-8972 |
| 中文摘要 | Ag-coated alpha-Al(2)O(3) powders were synthesized using silver electroless deposition process, which was carried out in an ammonia-based coating solution containing silver nitrate as a starting material. In the case of using pretreated alpha-Al(2)O(3) powders, a thin layer of Ag was coated on the alpha-Al(2)O(3) powders providing a core-shell structure. The thin layer of Ag in thickness had an amorphous structure of about 5 nm. Some crystalline Ag particles about 10 nm in diameter were also observed. However, in the case of using alpha-Al(2)O(3) powders that were not pretreated, large Ag particles about 100 nm were formed, although a core-shell structure was found on the surface of alpha-Al(2)O(3) powders. (c) 2004 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35028]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | G. M. Shi,J. K. Han,Z. D. Zhang,et al. Pretreatment effect on the synthesis of Ag-coated Al(2)O(3) powders by electroless deposition process[J]. Surface & Coatings Technology,2005,195(2-3):333-337. |
| APA | G. M. Shi,J. K. Han,Z. D. Zhang,H. Y. Song,&B. T. Lee.(2005).Pretreatment effect on the synthesis of Ag-coated Al(2)O(3) powders by electroless deposition process.Surface & Coatings Technology,195(2-3),333-337. |
| MLA | G. M. Shi,et al."Pretreatment effect on the synthesis of Ag-coated Al(2)O(3) powders by electroless deposition process".Surface & Coatings Technology 195.2-3(2005):333-337. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。