The oxidation behavior and mechanical performance of Ti60 alloy with enamel coating
文献类型：期刊论文
| 作者 | Y. M. Xiong ; S. L. Zhu ; F. H. Wang |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2005 |
| 卷号 | 190期号:2-3页码:195-199 |
| 关键词 | oxidation mechanics microhardness Ti60 alloy enamel coating high-temperature oxidation tial intermetallic compound resistance corrosion titanium improvement protection film |
| ISSN号 | 0257-8972 |
| 中文摘要 | In the present paper, the influence of enamel coating, compared to the traditional TiAlCr coating, on oxidation behavior and oxygen contamination of Ti60 alloy at 700 and 800 degreesC was studied. A continuous protective alumina scale formed on TiAlCr coating during oxidation at the two temperatures; but a rather heavy interdiffusion layer appeared at the interface of TiAlCr/Ti60 during oxidation at 800 degreesC. The uniform and dense enamel coating could provide excellent protectiveness to Ti60 due to its thermal chemical stability and good compatibility in terms of thermal expansion coefficient to the substrate Ti60 alloy. According to the microhardness measurement results, there exists a layer of contamination of about 30 gm into the alloy after the enamel was vitrified for 30 min at 900 degreesC in air; but the depth of oxygen contamination into the alloy changed little after oxidation for 1000 h at 600 degreesC. The strength and the elongation at ambient temperature of Ti60 alloy with enamel coating decreased about 7.4% and 3.4% in comparison to the original bare alloy, respectively. From the results, the enamel coating could protect Ti60 alloy from oxidation and oxygen embrittlement. (C) 2004 Published by Elsevier B.V. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35158]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. M. Xiong,S. L. Zhu,F. H. Wang. The oxidation behavior and mechanical performance of Ti60 alloy with enamel coating[J]. Surface & Coatings Technology,2005,190(2-3):195-199. |
| APA | Y. M. Xiong,S. L. Zhu,&F. H. Wang.(2005).The oxidation behavior and mechanical performance of Ti60 alloy with enamel coating.Surface & Coatings Technology,190(2-3),195-199. |
| MLA | Y. M. Xiong,et al."The oxidation behavior and mechanical performance of Ti60 alloy with enamel coating".Surface & Coatings Technology 190.2-3(2005):195-199. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。