Wetting behavior of Zr55Cu30Al10Ni5 melt on alumina
文献类型：期刊论文
| 作者 | Q. G. Xu ; H. F. Zhang ; Z. Q. Hu |
| 刊名 | Transactions of Nonferrous Metals Society of China
 |
| 出版日期 | 2005 |
| 卷号 | 15期号:1页码:45-50 |
| 关键词 | wetting interfacial reaction precursor film glass matrix composites metal |
| ISSN号 | 1003-6326 |
| 中文摘要 | The wetting behavior of molten Zr-55 Cu-30 Al-10 Ni-5 on Al2O3 was studied by the sessite drop method in high vacuum. The results show that wetting kinetic at 1163 K is composed of three stages: incubation, quasi-steady decrease and trend constant. Precursor film forms surrounding the wetting tip when wetting temperature is above 1163 K. Formation of precursor film is related to the change of triple tine configuration and results in good wettability. Chemical reaction dos not occur at the wetting interface. Al2O3 is an excellent reinforcement for Zr-55 Cu-30 Al-10 Ni-5 matrix composite in terms of wettability and reactivity. The kinetic relationship of spreading ratio with spreading time was also investigated. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35162]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Q. G. Xu,H. F. Zhang,Z. Q. Hu. Wetting behavior of Zr55Cu30Al10Ni5 melt on alumina[J]. Transactions of Nonferrous Metals Society of China,2005,15(1):45-50. |
| APA | Q. G. Xu,H. F. Zhang,&Z. Q. Hu.(2005).Wetting behavior of Zr55Cu30Al10Ni5 melt on alumina.Transactions of Nonferrous Metals Society of China,15(1),45-50. |
| MLA | Q. G. Xu,et al."Wetting behavior of Zr55Cu30Al10Ni5 melt on alumina".Transactions of Nonferrous Metals Society of China 15.1(2005):45-50. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。