Hot corrosion of an electrodeposited Ni-11 wt % Cr nanocomposite under molten Na2SO4-K2SO4-NaCl
文献类型：期刊论文
| 作者 | C. Zhang ; X. Peng ; J. Zhao ; F. Wang |
| 刊名 | Journal of the Electrochemical Society
 |
| 出版日期 | 2005 |
| 卷号 | 152期号:9页码:B321-B326 |
| 关键词 | high-temperature corrosion oxidation behavior coatings alloy scale oxides film 800-degrees-c sulfidation yttrium |
| ISSN号 | 0013-4651 |
| 中文摘要 | A Ni-Cr nanocomposite with an average Cr concentration of 11 (wt %) was deposited onto nickel plate by simultaneous electrodeposition of Ni and Cr nanoparticles from a nickel sulfate bath. The nanocomposite consisted of a nanocrystalline Ni matrix and dispersed Cr nanoparticles with a mean size of 33 nm. For comparison, two Ni-Cr alloys, one with similar Cr content (10 wt %) and the other with much higher Cr content (20 wt %), were prepared using electro-arc melting. Hot corrosion testing under molten Na2SO4-K2SO4-NaCl in air at 700 degrees C showed that rapid formation of a continuous chromia-rich scale is essential for hot corrosion protection. This was the case only for the nanocomposite. Internal sulfidation was observed for arc-melted alloys, but not for the nanocomposite. The results demonstrate that it was not primarily the Cr content but the unique structure of the nanocomposite that was responsible for its superior hot corrosion resistance. The protection mechanism lies in the fast formation of a continuous chromia scale on the nanocomposite, due to the easy nucleation of chromia on both chromium nanoparticles and abundant nickel grain boundaries, and then fast linking of the nuclei as a result of enhanced diffusion of Cr through those grain boundaries. (c) 2005 The Electrochemical Society. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35198]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | C. Zhang,X. Peng,J. Zhao,et al. Hot corrosion of an electrodeposited Ni-11 wt % Cr nanocomposite under molten Na2SO4-K2SO4-NaCl[J]. Journal of the Electrochemical Society,2005,152(9):B321-B326. |
| APA | C. Zhang,X. Peng,J. Zhao,&F. Wang.(2005).Hot corrosion of an electrodeposited Ni-11 wt % Cr nanocomposite under molten Na2SO4-K2SO4-NaCl.Journal of the Electrochemical Society,152(9),B321-B326. |
| MLA | C. Zhang,et al."Hot corrosion of an electrodeposited Ni-11 wt % Cr nanocomposite under molten Na2SO4-K2SO4-NaCl".Journal of the Electrochemical Society 152.9(2005):B321-B326. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。