Thermal stability of mechanically alloyed boride/Ti(50)Cu(18)Ni(22)Al(4)Sn(6) glassy alloy composites
文献类型：期刊论文
| 作者 | L. C. Zhang ; Z. Q. Shen ; J. Xu |
| 刊名 | Journal of Non-Crystalline Solids
 |
| 出版日期 | 2005 |
| 卷号 | 351期号:27-29页码:2277-2286 |
| 关键词 | bulk metallic-glass supercooled liquid region gas-atomized powders channel angular extrusion al-cu-ni matrix composites amorphous-alloys warm extrusion zrc particles high-strength |
| ISSN号 | 0022-3093 |
| 中文摘要 | The Ti(50)Cu(18)Ni(22)Al(4)Sn(6) multicomponent alloy was chosen as base alloy due to a complete glass formation under ball milling and a sizable supercooled liquid region, Delta T(x) = 66 K. The mixtures of prealloyed Ti(50)Cu(18)Ni(22)Al(4)Sn(6) fragments with CrB or TiB(2) particles up to 30 vol.% were mechanically milled to fabricate the boride/Ti-based glassy alloy composites. The structural features of the as-milled products were characterized using X-ray diffraction, transmission electron microscopy and differential scanning calorimetry. In the ball-milled composites, the CrB or TiB2 particles with sizes ranging around 10-200 nm are dispersed in the Ti-based glassy alloy matrix. Similar to the Ti(50)Cu(18)Ni(22)Al(4)Sn(6) glassy alloy without any borides, a well-defined glass transition temperature, T(g), and a wide supercooled liquid region, Delta T(x) are observed also for the boride-containing composites. Furthermore, the glass transition and thermal stability of supercooled liquid for the matrix alloy in the composites are dependent on the fraction of boride addition. In the case of CrB addition, the Delta T(x), value of glassy phase matrix was reduced due to a strong fraction dependence of the Tg than that of the T(x), remaining at about 60 K for boride fractions less than 15 vol.%. In contrast, both the T(g) and T(x) of the TiB(2)-containing composites were raised with increasing TiB(2) fraction up to 30 vol.%, resulting in no significant change for the AT,. (c) 2005 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35216]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. C. Zhang,Z. Q. Shen,J. Xu. Thermal stability of mechanically alloyed boride/Ti(50)Cu(18)Ni(22)Al(4)Sn(6) glassy alloy composites[J]. Journal of Non-Crystalline Solids,2005,351(27-29):2277-2286. |
| APA | L. C. Zhang,Z. Q. Shen,&J. Xu.(2005).Thermal stability of mechanically alloyed boride/Ti(50)Cu(18)Ni(22)Al(4)Sn(6) glassy alloy composites.Journal of Non-Crystalline Solids,351(27-29),2277-2286. |
| MLA | L. C. Zhang,et al."Thermal stability of mechanically alloyed boride/Ti(50)Cu(18)Ni(22)Al(4)Sn(6) glassy alloy composites".Journal of Non-Crystalline Solids 351.27-29(2005):2277-2286. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。