Morphology evolution of alumina scales formed on NiAl with and without 0.5 at.% Ag at 1273K
文献类型：期刊论文
| 作者 | X. J. Zhang ; W. T. Wu ; J. T. Guo ; Y. Niu |
| 刊名 | High Temperature Materials and Processes
 |
| 出版日期 | 2005 |
| 卷号 | 24期号:1页码:17-28 |
| 关键词 | beta-NiAl silver oxidation gamma-Al2O3 theta-Al2O3 alpha-Al2O3 transformation oxidation behavior transient oxidation intergranular oxidation isothermal oxidation ion-implantation growth-mechanism initial-stages base alloys coatings nickel |
| ISSN号 | 0334-6455 |
| 中文摘要 | The transient oxidation behavior of beta-NiAl and NiAl-0.5Ag in 1 atm O-2 at 1273K was studied by thermogravimetry, giving special emphasis to the evolution of the morphology of the oxide scale, especially for what concerns the transformation of transient aluminas into the stable alpha-Al2O3 form. The oxidation kinetics can be described as being composed of three different parabolic stages for NiAl-0.5Ag and of two stages for beta-NiAl. Three different oxide morphologies are observed for the two alloys at different oxidation times. The SEM and XRD results show that the transient oxidation can be divided into two main stages, including the initial formation of gamma-Al2O3, which transforms quickly into theta-Al2O3, and the subsequent transformation of theta-Al2O3 into alpha-Al2O3. A combination of the results by XRD, EDAX and SEM shows that silver promotes the transformation of theta-Al2O3 into alpha-Al2O3, which is faster on NiAl-0.5Ag than on beta-NiAl. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35235]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. J. Zhang,W. T. Wu,J. T. Guo,et al. Morphology evolution of alumina scales formed on NiAl with and without 0.5 at.% Ag at 1273K[J]. High Temperature Materials and Processes,2005,24(1):17-28. |
| APA | X. J. Zhang,W. T. Wu,J. T. Guo,&Y. Niu.(2005).Morphology evolution of alumina scales formed on NiAl with and without 0.5 at.% Ag at 1273K.High Temperature Materials and Processes,24(1),17-28. |
| MLA | X. J. Zhang,et al."Morphology evolution of alumina scales formed on NiAl with and without 0.5 at.% Ag at 1273K".High Temperature Materials and Processes 24.1(2005):17-28. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。