Punch-shear tests and size effects for evaluating the shear strength of machinable ceramics
文献类型：期刊论文
| 作者 | Y. W. Bao ; H. B. Zhang ; Y. C. Zhou |
| 刊名 | Zeitschrift Fur Metallkunde
 |
| 出版日期 | 2004 |
| 卷号 | 95期号:5页码:372-376 |
| 关键词 | punch-shear test shear strength size effects machinable ceramics liquid reaction synthesis elevated-temperatures ti3sic2 ti3alc2 carbide microstructure composites failure |
| ISSN号 | 0044-3093 |
| 中文摘要 | Various sample thicknesses and punch diameters were used in punch-shear tests for investigating the size effects in evaluating the shear strength of machinable ceramics. The ratio of the sample thickness to the punch diameter was defined as the relative thickness that strongly affects the measured shear strength in a certain range. It was found that there was a threshold value in the relative thicknesses (similar to0.1 for Ti3AlC2 and similar to0.13 for Ti3SiC2) above which the measured shear strength increased linearly with increasing thickness. The threshold provided a thickness-requirement for valid punch-shear tests, and stable shear strength was obtained under this requirement using 3 mm and 1.8 mm punch diameters, respectively. Experiments using various loading rates suggested that the shear strength measured by the punch-shear test was almost immune from the loading rates. The mechanism of the size effects was analysed through optical and SEM observations. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35309]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. W. Bao,H. B. Zhang,Y. C. Zhou. Punch-shear tests and size effects for evaluating the shear strength of machinable ceramics[J]. Zeitschrift Fur Metallkunde,2004,95(5):372-376. |
| APA | Y. W. Bao,H. B. Zhang,&Y. C. Zhou.(2004).Punch-shear tests and size effects for evaluating the shear strength of machinable ceramics.Zeitschrift Fur Metallkunde,95(5),372-376. |
| MLA | Y. W. Bao,et al."Punch-shear tests and size effects for evaluating the shear strength of machinable ceramics".Zeitschrift Fur Metallkunde 95.5(2004):372-376. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。