Fabrication of multifilament Bi-2223/Ag tapes by varying the lead content and calcination temperature of precursor powders
文献类型：期刊论文
| 作者 | C. H. Jiang ; J. M. Yoo ; J. W. Ko ; G. W. Qiao |
| 刊名 | Physica C-Superconductivity and Its Applications
 |
| 出版日期 | 2004 |
| 卷号 | 406期号:3-4页码:183-188 |
| 关键词 | Bi-2223/Ag. tapes precursor powders lead content calcination temperature critical-current density phase assemblage microstructure platelets j(c) |
| ISSN号 | 0921-4534 |
| 中文摘要 | A set of multifilament Bi-2223/Ag tapes were fabricated by varying the lead content and calcination temperature of starting precursors. The influence of precursor conditions on the phase formation, microstructure and J(c) property of Bi2223/Ag tapes were explored with XRD, DTA, SEM-EDS and transport current measurements. The results showed that the Pb content of 0.20 in the nominal composition of Bi1.8PbvSr2.0Ca3.0Cu3.0Oz is too low to lead to a fully formation of Bi-2223 phase in tapes compared with Pb content of 0.25 and 0.30. In addition, despite the Pb variations, the powders calcined at 820 degreesC resulted in the highest J(c) in final tapes against the powders calcined at 810 and 830 degreesC. The correlation between the transport property and the varied phase assemblages of precursors induced by lead and calcination temperature variations was discussed. (C) 2004 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35386]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | C. H. Jiang,J. M. Yoo,J. W. Ko,et al. Fabrication of multifilament Bi-2223/Ag tapes by varying the lead content and calcination temperature of precursor powders[J]. Physica C-Superconductivity and Its Applications,2004,406(3-4):183-188. |
| APA | C. H. Jiang,J. M. Yoo,J. W. Ko,&G. W. Qiao.(2004).Fabrication of multifilament Bi-2223/Ag tapes by varying the lead content and calcination temperature of precursor powders.Physica C-Superconductivity and Its Applications,406(3-4),183-188. |
| MLA | C. H. Jiang,et al."Fabrication of multifilament Bi-2223/Ag tapes by varying the lead content and calcination temperature of precursor powders".Physica C-Superconductivity and Its Applications 406.3-4(2004):183-188. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。