Sulfidation behavior of Fe-40Al sheet in H-2-H2S mixtures at high temperatures
文献类型：期刊论文
| 作者 | F. Q. Lang ; Z. M. Yu ; S. Gedevanishvili ; S. C. Deevi ; S. Hayashi ; T. Narita |
| 刊名 | Intermetallics
 |
| 出版日期 | 2004 |
| 卷号 | 12期号:5页码:469-475 |
| 关键词 | iron aluminides (based on FeAl) corrosion fe-al alloys corrosion behavior oxidation behavior iron aluminides sulfur vapor al2o3 scales 1273 k atmospheres |
| ISSN号 | 0966-9795 |
| 中文摘要 | The sulfidation behavior of a 200 mum thick Fe-40at.%Al sheet has been investigated at temperatures between 973 K and 1273 K in H-2-H2S mixtures with H,S contents of 0.052-9.7vol%. The Fe-40Al sheet exhibited excellent sulfidation resistance at temperatures below 1073 K in all the H2S-H-2 mixtures. This may be attributed to the formation of a thin alumina film on the surface of the Fe-40Al sheet during sulfidation, identified by AES analysis. At temperatures higher than 1173 K, the Fe-40Al sheet also exhibited good sulfidation resistance in the 0.052%H2S-H-2, mixture. and there was only a slight increase in mass gain with tempe rat Lire. This compares favorably with Fe-200-11Al (in at.%) foil which was severely sulfidized even at 973 K in the 0.052% H2S-H-2 mixture, and showed markedly increased mass gain with increased H2S content and temperature. (C) 2004 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35396]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | F. Q. Lang,Z. M. Yu,S. Gedevanishvili,et al. Sulfidation behavior of Fe-40Al sheet in H-2-H2S mixtures at high temperatures[J]. Intermetallics,2004,12(5):469-475. |
| APA | F. Q. Lang,Z. M. Yu,S. Gedevanishvili,S. C. Deevi,S. Hayashi,&T. Narita.(2004).Sulfidation behavior of Fe-40Al sheet in H-2-H2S mixtures at high temperatures.Intermetallics,12(5),469-475. |
| MLA | F. Q. Lang,et al."Sulfidation behavior of Fe-40Al sheet in H-2-H2S mixtures at high temperatures".Intermetallics 12.5(2004):469-475. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。