Microstructure evolution and low temperature superplasticity of ZK40 magnesium alloy subjected to ECAP

文献类型:期刊论文

作者L. Lin ; Z. Liu ; L. J. Chen ; T. Liu ; S. D. Wu
刊名Metals and Materials International
出版日期2004
卷号10期号:6页码:501-506
关键词magnesium alloys grain refinement superplasticity ECAP channel angular extrusion nonequilibrium grain-boundaries severe plastic-deformation mechanical-properties az91 magnesium
ISSN号1598-9623
中文摘要Microstructure evolution and superplastic behaviors of ZK40 magnesium alloy were investigated in the temperature range of 473similar to623 K. Transmission electron microscopy (TEM) was used to study the microstructure changes. After the alloy had been processed by equal channel angular pressing (ECAP) for one pass through the die, significant twinning was found to have Occurred, and the mean grain size was 5.6 mum. Finer grains were obtained after multi-pass ECAP, and the average grain size of the alloy ECAPed for three passes was as low as 0.8 mum; this alloy exhibited low temperature superplasticity at 473similar to523 K, and the elongations obtained at the initial strain rate of 1 x 10(-3) s(-1) were 260 % at 473 K and 612 % at 523 K. Corresponding values for the ZK40 alloy processed by ECAP for only one pass were 124 % at 473 K and 212 % at 523 K. Poor superplastic behavior of the ZK40 alloy processed by ECAP for only one pass was related to the long-range stresses associated with the non-equilibrium grain boundaries within the coarse grains. The incompatibility between the fine grains and the coarse grains was thought to be unfavorable to the improvement of superplasticity.
原文出处://WOS:000225797600001
公开日期2012-04-14
源URL[http://ir.imr.ac.cn/handle/321006/35446]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
L. Lin,Z. Liu,L. J. Chen,et al. Microstructure evolution and low temperature superplasticity of ZK40 magnesium alloy subjected to ECAP[J]. Metals and Materials International,2004,10(6):501-506.
APA L. Lin,Z. Liu,L. J. Chen,T. Liu,&S. D. Wu.(2004).Microstructure evolution and low temperature superplasticity of ZK40 magnesium alloy subjected to ECAP.Metals and Materials International,10(6),501-506.
MLA L. Lin,et al."Microstructure evolution and low temperature superplasticity of ZK40 magnesium alloy subjected to ECAP".Metals and Materials International 10.6(2004):501-506.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。