Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy
文献类型：期刊论文
| 作者 | J. R. Liu ; S. X. Li ; D. Li ; R. Yang |
| 刊名 | Materials Science and Technology
 |
| 出版日期 | 2004 |
| 卷号 | 20期号:10页码:1266-1272 |
| 关键词 | isothermal and thermomechanical fatigue high temperature titanium alloys fatigue life aisi-304l stainless-steel imi 834 deformation-behavior damage mechanisms superalloy creep |
| ISSN号 | 0267-0836 |
| 中文摘要 | Isothermal and thermomechanical fatigue (TMF) behaviour (including cyclic stress response and number of cycles to failure) of a Ti-5(.)6Al-4(.)8Sn-2(.)0Zr-1(.)0-Mo-0(.)32Si-0(.)8Nd (wt-%) hightemperature titanium alloy was examined. The purpose of the present investigation was to understand the effect of temperature fluctuation on the cyclic behaviour and fatigue life of this alloy and to test the suitability of lifetime prediction based on isothermal laboratory data. The results indicated that both the level of peak stress and fatigue life were decreasing with increasing test temperature from 400degreesC to 650degreesC in isothermal fatigue (IF) tests. In TMF tests run between 400degreesC and 600degreesC, the peak stresses corresponding to 600degreesC coincide well with that found in IF tests run at 600degreesC, while a slight increase in cyclic hardening was found for peak stress corresponding to 400degreesC compared to that found in a 400degreesC/IF test. This increase in cyclic hardening became more pronounced when the maximum temperature increased to 650degreesC. Fatigue life in 'out of phase' (OP) condition was found to be shorter than under an equivalent 'in phase' (IP) condition, and this gap increased with decreasing mechanical strain amplitude. The results indicate that lifetime prediction based on isothermal laboratory data may lead to non-conservative results if thermal fluctuations are present in components made of the present alloy. |
| 原文出处 | |
| 公开日期 | 2012-04-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/35460]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. R. Liu,S. X. Li,D. Li,et al. Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy[J]. Materials Science and Technology,2004,20(10):1266-1272. |
| APA | J. R. Liu,S. X. Li,D. Li,&R. Yang.(2004).Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy.Materials Science and Technology,20(10),1266-1272. |
| MLA | J. R. Liu,et al."Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy".Materials Science and Technology 20.10(2004):1266-1272. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。